Diamond Polymers NPP25-0120B GF15 Glass Filled Copolymer Polypropylene
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.02 g/cc | 0.0368 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.014 – 0.018 cm/cm | 0.014 – 0.018 in/in | ASTM D955 |
| Melt Flow | 0.90 g/10 min
@Load 2.16 kg,
Temperature 230 °C |
0.90 g/10 min
@Load 4.76 lb,
Temperature 446 °F |
ASTM D1238 |
| Ash | 15 % | 15 % | ASTM D5630 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 31.0 MPa | 4500 psi | chs 2.0 in/min; ASTM D638 |
| Elongation at Yield | 0.60 % | 0.60 % | chs 2.0 in/min; ASTM D638 |
| Tensile Modulus | 3.007 GPa | 436.1 ksi | chs 2.0 in/min; ASTM D638 |
| Flexural Strength | 44.4 MPa
@Thickness 3.17 mm
|
6440 psi
@Thickness 0.125 in
|
chs 0.05 in/min; SL 2 inches; ASTM D790 |
| Flexural Modulus | 2.983 GPa
@Thickness 3.17 mm
|
432.6 ksi
@Thickness 0.125 in
|
chs 0.05 in/min; SL 2 inches; ASTM D790 |
| Izod Impact, Notched | 1.816 J/cm
@Thickness 3.17 mm
|
3.402 ft-lb/in
@Thickness 0.125 in
|
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 137 °C | 279 °F | 0.125″;; ASTM D648 |
| Vicat Softening Point | 152 °C
@Load 1.00 kg
|
306 °F
@Load 2.20 lb
|
120°C/hr; ASTM D1525 |