Aaron Industries AAROPRENE® TFIPP 2040 High Impact Talc Filled Polypropylene
| Manufacturer | Aaron Industries Corporation |
| Trade Name | AAROPRENE® TFIPP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
AAROPRENE® TFIPP 2000 Series Reinforced CompoundsMelt flow index may be specified. Color may be specified.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.24 g/cc | 1.24 g/cc | ASTM D792 |
| Filler Content | 40 % | 40 % | Talc; ASTM D2584 |
| Linear Mold Shrinkage | 0.010 cm/cm | 0.010 in/in | ASTM D955 |
| Melt Flow | 8.0 – 12 g/10 min
@Load 2.16 kg,
Temperature 230 °C |
8.0 – 12 g/10 min
@Load 4.76 lb,
Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 26.6 MPa | 3860 psi | ASTM D638 |
| Flexural Modulus | 2.83 GPa | 410 ksi | ASTM D790 |
| Izod Impact, Notched | 0.481 J/cm | 0.900 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 124 °C | 255 °F | ASTM D648 |