Premix Thermoplastics PRE-ELEC® PP 1391 Conductive Thermoplastic Compound
| Manufacturer | Premix Thermoplastics Inc. |
| Trade Name | PRE-ELEC® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
PRE-ELEC® PP 1391 is a conductive thermoplastic compound based on polypropylene. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity PRE-ELEC® PP 1391 has excellent mechanical properties, high melt strength and is easy to extrude.Applications: Extrusion of corrugated sheet.Processing: PRE-ELEC® PP 1391 compound can be extruded in the machines using normal processing conditions as with polypropylene.Test Specimen: 10[mm] wide moulded rodInformation from Premix OY
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.980 g/cc | 0.0354 lb/in³ | |
| Thickness | 102 microns | 4.00 mil | |
| Linear Mold Shrinkage | 0.013 – 0.019 cm/cm | 0.013 – 0.019 in/in | ISO 294-4 |
| Melt Flow | 0.40 g/10 min
@Load 2.16 kg,
Temperature 230 °C |
0.40 g/10 min
@Load 4.76 lb,
Temperature 446 °F |
ISO 1133 |
| 2.0 g/10 min
@Load 5.00 kg,
Temperature 230 °C |
2.0 g/10 min
@Load 11.0 lb,
Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 99 | 99 | ISO 868 |
| Hardness, Shore D | 74 | 74 | ISO 868 |
| Film Tensile Strength at Yield, MD | 23.0 MPa
@Thickness 0.400 mm
|
3340 psi
@Thickness 0.0157 in
|
ISO 527 |
| Film Tensile Strength at Yield, TD | 22.0 MPa
@Thickness 0.400 mm
|
3190 psi
@Thickness 0.0157 in
|
ISO 527 |
| Film Elongation at Break, MD | 500 %
@Thickness 0.400 mm
|
500 %
@Thickness 0.0157 in
|
ISO 527 |
| Film Elongation at Break, TD | 500 %
@Thickness 0.400 mm
|
500 %
@Thickness 0.0157 in
|
ISO 527 |
| Film Elongation at Yield, MD | 18 %
@Thickness 0.400 mm
|
18 %
@Thickness 0.0157 in
|
ISO 527 |
| Film Elongation at Yield, TD | 18 %
@Thickness 0.400 mm
|
18 %
@Thickness 0.0157 in
|
ISO 527 |
| Flexural Modulus | 1.40 GPa | 203 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | NB
@Thickness 4.00 mm,
Temperature 23.0 °C |
NB
@Thickness 0.157 in,
Temperature 73.4 °F |
ISO 180 |
| NB
@Thickness 4.00 mm,
Temperature -20.0 °C |
NB
@Thickness 0.157 in,
Temperature -4.00 °F |
ISO 180 | |
| Izod Impact, Unnotched (ISO) | NB
@Thickness 4.00 mm,
Temperature 23.0 °C |
NB
@Thickness 0.157 in,
Temperature 73.4 °F |
ISO 180 |
| NB
@Thickness 4.00 mm,
Temperature -20.0 °C |
NB
@Thickness 0.157 in,
Temperature -4.00 °F |
ISO 180 | |
| Charpy Impact Unnotched | NB
@Thickness 102 mm,
Temperature 23.0 °C |
NB
@Thickness 4.00 in,
Temperature 73.4 °F |
ISO 179 |
| NB
@Thickness 102 mm,
Temperature -20.0 °C |
NB
@Thickness 4.00 in,
Temperature -4.00 °F |
ISO 179 | |
| Charpy Impact, Notched | 2.50 J/cm²
@Thickness 102 mm,
Temperature -20.0 °C |
11.9 ft-lb/in²
@Thickness 4.00 in,
Temperature -4.00 °F |
ISO 179 |
| 5.00 J/cm²
@Thickness 102 mm,
Temperature 23.0 °C |
23.8 ft-lb/in²
@Thickness 4.00 in,
Temperature 73.4 °F |
ISO 179 | |
| Film Tensile Strength at Break, MD | 25.0 MPa
@Thickness 0.400 mm
|
3630 psi
@Thickness 0.0157 in
|
ISO 527 |
| Film Tensile Strength at Break, TD | 23.0 MPa
@Thickness 0.400 mm
|
3340 psi
@Thickness 0.0157 in
|
ISO 527 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 90.0 °C | 194 °F | 75/Method Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 53.0 °C | 127 °F | 75/Method Af |
| Vicat Softening Point | 151 °C | 304 °F | ISO 306/A50 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | <= 1000 ohm-cm
@Thickness 0.400 mm
|
<= 1000 ohm-cm
@Thickness 0.0157 in
|
ISO D-257 |
| Surface Resistance | <= 10000 ohm
@Thickness 0.400 mm
|
<= 10000 ohm
@Thickness 0.0157 in
|
ISO IEC 61340-5-1 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 210 °C | 410 °F | Cylinder |
| 230 °C | 446 °F | Die | |
| Zone 2 | 220 °C | 428 °F | Cylinder |
| 230 °C | 446 °F | Die | |
| Zone 3 | 220 °C | 428 °F | Die |
| 220 °C | 428 °F | Cylinder | |
| Zone 4 | 230 °C | 446 °F | Die |
| 230 °C | 446 °F | Cylinder | |
| Zone 5 | 230 °C | 446 °F | Die |
| 230 °C | 446 °F | Cylinder | |
| Roll Temperature | 60.0 °C | 140 °F | 3rd Roll |
| 80.0 °C | 176 °F | 2nd Roll | |
| 90.0 °C | 194 °F | 1st Roll | |
| Drying Temperature | 60.0 – 80.0 °C | 140 – 176 °F | Pre-drying |
| Dry Time | 2 – 4 hour | 2 – 4 hour | |
| Shelf Life | 12.0 Month | 12.0 Month | Normal Storing Conditions |