BASF Neopolen® P 8225 K 0.025 g/cc Core density; Expanded Polypropylene (Europe)
| Manufacturer | BASF |
| Trade Name | Neopolen® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Description: Neopolen® P 8225 K is expanded Polypropylene supplied in the form of beads. The cells are largely closed.Physical properties of moldings made from Neopolen® P 8225 K.Note: In order to measure the physical properties, parts with dimensions 300x200x60 mm were molded on a machine typical for the EPP industry under standard conditions. The properties can vary depending on part geometry and processing parameters.Information provided by BASF
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.0190 – 0.0232 g/cc | 0.000686 – 0.000838 lb/in³ | |
| Density | 0.0250 g/cc | 0.000903 lb/in³ | ISO 845 |
| Water Absorption | <= 1.0 %
@Time 86400 sec
|
<= 1.0 %
@Time 24.0 hour
|
DIN 53428 |
| Particle Size | >= 2000 µm | >= 2000 µm | |
| <= 5500 µm | <= 5500 µm |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 0.380 MPa | 55.1 psi | DIN EN ISO 1798 |
| Elongation at Break | 38 % | 38 % | DIN EN ISO 1798 |
| Compressive Strength | 0.0900 MPa
@Strain 10.0 %
|
13.1 psi
@Strain 10.0 %
|
ISO 844 |
| 0.110 MPa
@Strain 25.0 %
|
16.0 psi
@Strain 25.0 %
|
ISO 844 | |
| 0.190 MPa
@Strain 50.0 %
|
27.6 psi
@Strain 50.0 %
|
ISO 844 | |
| Compression Set | 30 %
@Temperature 23.0 °C,
Time 79200 sec |
30 %
@Temperature 73.4 °F,
Time 22.0 hour |
50% RH; 24h after stress release; DIN EN ISO 1856 (Procedure C) |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 0.0360 W/m-K | 0.250 BTU-in/hr-ft²-°F | DIN 52612 |