Samsung Cheil Industries Starex® TF-0956 HI-PMMA
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Starex® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Information provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.16 g/cc | 1.16 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0040 – 0.0080 cm/cm
@Thickness 3.20 mm
|
0.0040 – 0.0080 in/in
@Thickness 0.126 in
|
ASTM D955 |
| Melt Flow | 3.0 g/10 min
@Load 3.80 kg,
Temperature 230 °C |
3.0 g/10 min
@Load 8.38 lb,
Temperature 446 °F |
ASTM D1238 |
| 7.0 g/10 min
@Load 10.0 kg,
Temperature 220 °C |
7.0 g/10 min
@Load 22.0 lb,
Temperature 428 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 115 | 115 | ASTM D785 |
| Tensile Strength, Yield | 52.0 MPa | 7540 psi | 5 mm/min; ASTM D638 |
| Flexural Strength | 72.6 MPa | 10500 psi | 2.8 mm/min; ASTM D790 |
| Flexural Modulus | 1.96 GPa | 284 ksi | 2.8 mm/min; ASTM D790 |
| Izod Impact, Notched | 0.441 J/cm
@Thickness 6.35 mm
|
0.827 ft-lb/in
@Thickness 0.250 in
|
ASTM D256 |
| 0.490 J/cm
@Thickness 3.17 mm
|
0.918 ft-lb/in
@Thickness 0.125 in
|
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 78.0 °C
@Thickness 6.40 mm
|
172 °F
@Thickness 0.252 in
|
ASTM D648 |
| Vicat Softening Point | 93.0 °C | 199 °F | B/50; ISO R306 |
| Flammability, UL94 | HB
@Thickness 1.50 – 3.00 mm
|
HB
@Thickness 0.0591 – 0.118 in
|