Samsung Cheil Industries Starex® TF-0959 T HI-PMMA
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Starex® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Information provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.17 g/cc | 1.17 g/cc | ASTM D792 |
| Melt Flow | 16 g/10 min
@Load 10.0 kg,
Temperature 220 °C |
16 g/10 min
@Load 22.0 lb,
Temperature 428 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 117 | 117 | ASTM D785 |
| Tensile Strength, Yield | 54.9 MPa | 7970 psi | 5 mm/min; ASTM D638 |
| Flexural Strength | 79.4 MPa | 11500 psi | 2.8 mm/min; ASTM D790 |
| Flexural Modulus | 2.31 GPa | 336 ksi | 2.8 mm/min; ASTM D790 |
| Izod Impact, Notched | 2.45 J/cm
@Thickness 6.35 mm
|
4.59 ft-lb/in
@Thickness 0.250 in
|
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 77.0 °C
@Thickness 6.40 mm
|
171 °F
@Thickness 0.252 in
|
ASTM D648 |
| Vicat Softening Point | 92.0 °C | 198 °F | B/50; ISO R306 |
| Flammability, UL94 | HB
@Thickness 1.50 – 3.00 mm
|
HB
@Thickness 0.0591 – 0.118 in
|
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 0.50 %
@Thickness 2.50 mm
|
0.50 %
@Thickness 0.0984 in
|
ASTM D1003 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Pencil Hardness | 3H | 500g, JIS K 5401 |