DuPont™ Clysar® EHC Polyolefin Shrink Packaging Film, 75 Gauge (discontinued **)
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Data provided by DuPont Packaging Polymers.A biaxially oriented, heat-shrinkable copolymer film. It is a polypropylene and polyethylene-based film that is predominantly polypropylene. Used when excellent optics, high shrink force, and superb sheet flatness are essential. An excellent choice for doing multi-packs, high-speed applications, and static sealing.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Oxygen Transmission | 97.0 cc-mm/m²-24hr-atm | 246 cc-mil/100 in²-24hr-atm | or 5100 cc/m²-24hr-atm for the film. ASTM D3985 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 130 % | 130 % | Average; ASTM D882 |
| Modulus of Elasticity | 0.770 GPa | 112 ksi | (stiffness), ASTM D882 |
| Coefficient of Friction, Dynamic | 0.40 | 0.40 | ASTM D1894 |
| Elmendorf Tear Strength MD | 6.0 g | 6.0 g | Orientation not specified; ASTM D1922 |
| Seal Strength | 2800 g/25 mm | 2800 g/in | F-88-68(73) |
| Film Tensile Strength at Break, MD | 131 MPa | 19000 psi | ASTM D882 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 1.2 % | 1.2 % | |
| Gloss | 130 % | 130 % |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 177 – 232 °C | 351 – 450 °F | Optimum Tunnel temperature range. |