EVALCA EVAL® LC-L101A Ethylene Vinyl Alcohol Copolymer Resin (discontinued **)
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
27 mol % Ethylene.Data provided by EVALCA. Applications: Blown film, melt phase forming. Highest gas barrier EVOH available. EVOH is used in packaging applications because of its outstanding gas barrier properties.EVAL™ is now produced as a part of the Kuraray product line.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | ASTM D1505 |
| Moisture Vapor Transmission | 3.10 cc-mm/m²-24hr-atm | 7.87 cc-mil/100 in²-24hr-atm | 40°C, 90% RH |
| Oxygen Transmission | 0.00400 cc-mm/m²-24hr-atm | 0.0102 cc-mil/100 in²-24hr-atm | 20°C; 65% RH; Permeability increases significantly at higher moisture content. |
| Melt Flow | 3.9 g/10 min
@Load 2.16 kg,
Temperature 210 °C |
3.9 g/10 min
@Load 4.76 lb,
Temperature 410 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 104 | 104 | ASTM D785 |
| Tensile Strength, Yield | 94.0 MPa | 13600 psi | 10%/min. ASTM D638 |
| Film Elongation at Break, MD | 200 % | 200 % | Orientation not specified; ASTM D882 |
| Elongation at Yield | 6.0 % | 6.0 % | 10%/min. ASTM D638 |
| Modulus of Elasticity | 3.10 GPa | 450 ksi | Youngs Modulus, ASTM D638, 10%/min. |
| Flexural Yield Strength | 150 MPa | 21800 psi | Bending Strength; ASTM D790 |
| Flexural Modulus | 4.70 GPa | 682 ksi | Bending Elasticity; ASTM D790 |
| Izod Impact, Notched | 0.600 J/cm | 1.12 ft-lb/in | ASTM D256 |
| Film Tensile Strength at Break, MD | 72.0 MPa | 10400 psi | Orientation not specified; ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 40.0 µm/m-°C | 22.2 µin/in-°F | Below Tg |
| 105 µm/m-°C | 58.3 µin/in-°F | Above Tg | |
| Specific Heat Capacity | 2.40 J/g-°C | 0.574 BTU/lb-°F | |
| Thermal Conductivity | 0.340 W/m-K | 2.36 BTU-in/hr-ft²-°F | For EVAL F101 |
| Melting Point | 191 °C | 376 °F | DSC |
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | For EP-F101 |
| Glass Transition Temp, Tg | 72.0 °C | 162 °F | Dynamic Viscoelasticity |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 1.8 % | 1.8 % | Film; ASTM D1003 |
| Gloss | 85 % | 85 % | 45°; Film; ASTM D2457 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 5.6 | 5.6 | Frequency Not Specified |
| Dissipation Factor | 0.18 | 0.18 | Frequency Not Specified |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | <= 240 °C | <= 464 °F |