Inno-Comp INNOPOL® CS 1-3810 10% Glass-Fiber-Filled Polypropylene Homopolymer
| Manufacturer | Inno-Comp Ltd |
| Trade Name | INNOPOL® CS |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
INNOPOL® CS 1-3810 is a 10% glass-fiber-filled polypropylene homopolymer compound. This grade is available in natural and custom colored form.INNOPOL® CS 1-3810 is recommended for producing injection molded products, where the required properties are high strength and stiffness.All information provided by INNO-COMP.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.970 g/cc
@Temperature 23.0 °C
|
0.0350 lb/in³
@Temperature 73.4 °F
|
ISO 1183 |
| Linear Mold Shrinkage | 0.0090 – 0.017 cm/cm | 0.0090 – 0.017 in/in | ISO 294-4:1997 |
| Melt Flow | 8.0 g/10 min
@Load 2.16 kg,
Temperature 230 °C |
8.0 g/10 min
@Load 4.76 lb,
Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 40.0 MPa | 5800 psi | 50 mm/min; ISO 527-1,-2 |
| Elongation at Yield | 5.0 % | 5.0 % | 50 mm/min; ISO 527-1,-2 |
| Tensile Modulus | 2.50 GPa | 363 ksi | ISO 527-1,-2 |
| Charpy Impact, Notched | 0.230 J/cm²
@Temperature -20.0 °C
|
1.09 ft-lb/in²
@Temperature -4.00 °F
|
ISO 179/1eA |
| 0.350 J/cm²
@Temperature 23.0 °C
|
1.67 ft-lb/in²
@Temperature 73.4 °F
|
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Flammability, UL94 | HB
@Thickness 1.60 mm
|
HB
@Thickness 0.0630 in
|
FMVSS 302 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Automotive Materials | Pass | FMVSS 302 |
| Color | Natural |