Lucent Polymers GPP-210 Polypropylene, 10% Glass Fiber Reinforced, Chemically Coupled, Impact Modified
| Manufacturer | Lucent Polymers |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Melt Flow Adjustable for ApplicationAdd “U” for UV StabilizedAdd “H” for Heat StabilizedInformation provided by Lucent Polymers, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.980 g/cc | 0.980 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0080 cm/cm
@Thickness 3.17 mm
|
0.0080 in/in
@Thickness 0.125 in
|
1/8″ Section |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 42.76 MPa | 6202 psi | ASTM D638 |
| Elongation at Break | 7.0 % | 7.0 % | ASTM D638 |
| Flexural Strength | 60.69 MPa | 8802 psi | ASTM D790 |
| Flexural Modulus | 1.897 GPa | 275.1 ksi | ASTM D790 |
| Izod Impact, Notched | 0.961 J/cm
@Thickness 3.17 mm
|
1.80 ft-lb/in
@Thickness 0.125 in
|
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C | 230 °F | ASTM D648 |