LATI Latene® EP 22UVH2 MX/25 PP Copolymer, Mineral Reinforced
| Manufacturer | LATI |
| Trade Name | Latene® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Polypropylene copolymer (PPc) based compound. UV stabilized. Improved thermal stabilization. Special mineral filler. Very good surface appearance. Good elongation.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | |
| Linear Mold Shrinkage, Flow | 0.011 – 0.014 cm/cm | 0.011 – 0.014 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0115 – 0.0145 cm/cm | 0.0115 – 0.0145 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Elongation at Break | >= 100 %
@Temperature 23.0 °C
|
>= 100 %
@Temperature 73.4 °F
|
|
| >= 100 %
@Temperature 60.0 °C
|
>= 100 %
@Temperature 140 °F
|
||
| >= 100 %
@Temperature 90.0 °C
|
>= 100 %
@Temperature 194 °F
|
||
| Elongation at Yield | 8.0 %
@Temperature 23.0 °C
|
8.0 %
@Temperature 73.4 °F
|
|
| 10 %
@Temperature 60.0 °C
|
10 %
@Temperature 140 °F
|
||
| Tensile Modulus | 0.500 GPa
@Temperature 90.0 °C
|
72.5 ksi
@Temperature 194 °F
|
|
| 1.00 GPa
@Temperature 60.0 °C
|
145 ksi
@Temperature 140 °F
|
||
| 2.50 GPa
@Temperature 23.0 °C
|
363 ksi
@Temperature 73.4 °F
|
||
| Charpy Impact Unnotched | 10.0 J/cm² | 47.6 ft-lb/in² | |
| Charpy Impact, Notched | 1.00 J/cm² | 4.76 ft-lb/in² |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 110 °C | 230 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 105 °C | 221 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | |
| Vicat Softening Point | 80.0 °C
@Load 5.00 kg
|
176 °F
@Load 11.0 lb
|
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | 400 V | 400 V | A solution |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 200 – 240 °C | 392 – 464 °F | |
| Mold Temperature | 40.0 – 60.0 °C | 104 – 140 °F | |
| Drying Temperature | 80.0 – 90.0 °C
@Time 10800 sec
|
176 – 194 °F
@Time 3.00 hour
|
| Descriptive Properties | Value | Comments |
|---|---|---|
| ISO Shrinkage – Pressure | 60 MPa |