Borealis Daplen™ EE137AI Polypropylene Compound 10% Mineral Filled
| Manufacturer | Borealis |
| Trade Name | Daplen™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Daplen EE137AI is a 10% mineral filled grade intended for injection molding. EE137AI has been developed especially for the car industry, to be used in interior parts where high scratch resistance is a necessity. EE138AI offers good balance in stiffness/impact strength and has very good scratch resistance.Daplen EE137AI has been developed especially for dashboards, pillar trims, door panels and pockets, and other automotive interior parts.Information provided by the Manufacturer.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.960 g/cc | 0.0347 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0011 cm/cm | 0.0011 in/in | Borealis Method |
| Melt Flow | 12 g/10 min
@Load 2.16 kg,
Temperature 230 °C |
12 g/10 min
@Load 4.76 lb,
Temperature 446 °F |
ISO 1133 |
| 45 g/10 min
@Load 5.00 kg,
Temperature 230 °C |
45 g/10 min
@Load 11.0 lb,
Temperature 446 °F |
ISO 1133 |
\
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 42.0 MPa | 6090 psi | H385/30; ISO 2039 |
| Tensile Strength, Yield | 20.99 MPa | 3045 psi | At 50 mm/min; ISO 527-2 |
| Elongation at Yield | 6.0 % | 6.0 % | At 50 mm/min; ISO 527-2 |
| Tensile Modulus | 1.85 GPa | 268 ksi | At 1 mm/min; ISO 527-2 |
| Flexural Modulus | 1.70 GPa | 247 ksi | At 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 25.0 kJ/m² | 11.9 ft-lb/in² | ISO 180/1A |
| 5.00 kJ/m²
@Temperature 0.000 °C
|
2.38 ft-lb/in²
@Temperature 32.0 °F
|
ISO 180/1A | |
| Charpy Impact Unnotched | 16.0 J/cm² | 76.1 ft-lb/in² | ISO 179/1eU |
| 6.00 J/cm²
@Temperature -20.0 °C
|
28.6 ft-lb/in²
@Temperature -4.00 °F
|
ISO 179/1eU | |
| Charpy Impact, Notched | 2.00 J/cm² | 9.52 ft-lb/in² | ISO 179/1eA |
| 0.450 J/cm²
@Temperature -20.0 °C
|
2.14 ft-lb/in²
@Temperature -4.00 °F
|
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | ISO 75-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | ISO 75-2 |
| Vicat Softening Point | 54.0 °C | 129 °F | B (50N); ISO 306 |
| 136 °C | 277 °F | A (10N); ISO 306 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 220 – 260 °C | 428 – 500 °F | |
| Mold Temperature | 30.0 – 50.0 °C | 86.0 – 122 °F |