ExxonMobil AP3AW Polypropylene Impact Copolymer
Manufacturer | Exxon Chemical |
Trade Name | |
Port | Shanghai port,China |
Trade Terms | FOB, CFR, CIF |
Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Product Description: A UV stabilized medium impact copolymer resin designed for automotive battery cases.Availability: Asia Pacific Features:Good UV ResistanceHigh StiffnessLow WarpageMedium FlowMedium Impact ResistanceNucleated Uses: Automotive ApplicationsAutomotive Under the HoodBattery Cases Processing Method: Injection MoldingInformation provided by ExxonMobil
Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 0.900 g/cc | 0.0325 lb/in³ | ExxonMobil Method |
Melt Flow | 10 g/10 min
@Load 2.16 kg,
Temperature 230 °C |
10 g/10 min
@Load 4.76 lb,
Temperature 446 °F |
ASTM D1238 |
Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 25.7 MPa | 3730 psi | ISO 527-2/50 |
27.1 MPa | 3930 psi | 2.0 in/min; ASTM D638 | |
Elongation at Yield | 5.6 % | 5.6 % | 2.0 in/min; ASTM D638 |
5.7 % | 5.7 % | ISO 527-2/50 | |
Tensile Modulus | 1.50 GPa | 218 ksi | ISO527-2/1 |
Flexural Modulus | 1.34 GPa | 194 ksi | 0.079 in/min; ISO 178 |
Flexural Modulus, 1% Secant | 1340 MPa | 194000 psi | 0.05 in/min; ASTM D790A |
1520 MPa | 220000 psi | 0.5 in/min; ASTM D790B | |
Izod Impact, Notched | 0.352 J/cm
@Temperature -17.8 °C
|
0.660 ft-lb/in
@Temperature 0.000 °F
|
ASTM D256A |
0.908 J/cm
@Temperature 22.8 °C
|
1.70 ft-lb/in
@Temperature 73.0 °F
|
ASTM D256A | |
Izod Impact, Notched (ISO) | 3.36 kJ/m²
@Temperature -40.0 °C
|
1.60 ft-lb/in²
@Temperature -40.0 °F
|
ISO 180/1A |
4.41 kJ/m²
@Temperature -17.8 °C
|
2.10 ft-lb/in²
@Temperature 0.000 °F
|
ISO 180/1A | |
8.82 kJ/m²
@Temperature 22.8 °C
|
4.20 ft-lb/in²
@Temperature 73.0 °F
|
ISO 180/1A | |
Charpy Impact, Notched | 0.315 J/cm²
@Temperature -30.0 °C
|
1.50 ft-lb/in²
@Temperature -22.0 °F
|
ISO 179/1eA |
0.399 J/cm²
@Temperature -20.0 °C
|
1.90 ft-lb/in²
@Temperature -4.00 °F
|
ISO 179/1eA | |
0.504 J/cm²
@Temperature 0.000 °C
|
2.40 ft-lb/in²
@Temperature 32.0 °F
|
ISO 179/1eA | |
0.987 J/cm²
@Temperature 22.8 °C
|
4.70 ft-lb/in²
@Temperature 73.0 °F
|
ISO 179/1eA | |
Gardner Impact | 18.1 J
@Thickness 3.17 mm,
Temperature -28.9 °C |
13.3 ft-lb
@Thickness 0.125 in,
Temperature -20.0 °F |
Geometry GC; ASTM D5420 |
Thermal Properties | Metric | English | Comments |
---|---|---|---|
Deflection Temperature at 0.46 MPa (66 psi) | 92.8 °C | 199 °F | ISO 75-2/Bf |
99.4 °C | 211 °F | Unannealed; ASTM D648 | |
116 °C | 241 °F | Annealed; ASTM D648 | |
Deflection Temperature at 1.8 MPa (264 psi) | 53.3 °C | 128 °F | ISO 75-2/A |