This property data is a summary of similar materials in the MatWeb database for the category “Glass Reinforced, Modified SMA”. Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.15 – 1.35 g/cc | 0.0415 – 0.0488 lb/in³ | Average value: 1.21 g/cc Grade Count:8 |
| Filler Content | 12.0 – 30.0 % | 12.0 – 30.0 % | Average value: 17.4 % Grade Count:5 |
| Linear Mold Shrinkage | 0.00100 – 0.00500 cm/cm | 0.00100 – 0.00500 in/in | Average value: 0.00269 cm/cm Grade Count:8 |
| Melt Flow | 0.200 – 1.10 g/10 min | 0.200 – 1.10 g/10 min | Average value: 0.660 g/10 min Grade Count:5 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 106 – 114 | 106 – 114 | Average value: 111 Grade Count:3 |
| Tensile Strength, Ultimate | 55.0 – 103 MPa | 7980 – 14900 psi | Average value: 71.5 MPa Grade Count:8 |
| Elongation at Break | 2.00 – 3.00 % | 2.00 – 3.00 % | Average value: 2.67 % Grade Count:3 |
| Elongation at Yield | 1.70 – 2.40 % | 1.70 – 2.40 % | Average value: 2.14 % Grade Count:5 |
| Modulus of Elasticity | 4.20 – 8.20 GPa | 609 – 1190 ksi | Average value: 5.46 GPa Grade Count:5 |
| Flexural Yield Strength | 83.0 – 166 MPa | 12000 – 24100 psi | Average value: 109 MPa Grade Count:8 |
| Flexural Modulus | 4.00 – 10.6 GPa | 580 – 1540 ksi | Average value: 5.66 GPa Grade Count:8 |
| Izod Impact, Notched | 0.750 – 0.960 J/cm | 1.41 – 1.80 ft-lb/in | Average value: 0.873 J/cm Grade Count:3 |
| Izod Impact, Unnotched | 2.67 – 3.84 J/cm | 5.00 – 7.19 ft-lb/in | Average value: 3.10 J/cm Grade Count:3 |
| Izod Impact, Notched (ISO) | 7.80 – 11.4 kJ/m² | 3.71 – 5.42 ft-lb/in² | Average value: 9.50 kJ/m² Grade Count:5 |
| 4.60 – 9.70 kJ/m²
@Temperature -40.0 – -40.0 °C
|
2.19 – 4.62 ft-lb/in²
@Temperature -40.0 – -40.0 °F
|
Average value: 6.98 kJ/m² Grade Count:5 | |
| Charpy Impact Unnotched | 1.84 – 3.36 J/cm² | 8.76 – 16.0 ft-lb/in² | Average value: 2.64 J/cm² Grade Count:5 |
| Charpy Impact, Notched | 0.770 – 1.38 J/cm² | 3.66 – 6.57 ft-lb/in² | Average value: 1.05 J/cm² Grade Count:5 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 43.2 – 59.4 µm/m-°C | 24.0 – 33.0 µin/in-°F | Average value: 51.8 µm/m-°C Grade Count:5 |
| Deflection Temperature at 0.46 MPa (66 psi) | 120 – 132 °C | 248 – 270 °F | Average value: 126 °C Grade Count:3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 115 – 124 °C | 239 – 255 °F | Average value: 120 °C Grade Count:8 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 227 – 288 °C | 440 – 550 °F | Average value: 261 °C Grade Count:5 |
| Melt Temperature | 232 – 288 °C | 450 – 550 °F | Average value: 262 °C Grade Count:8 |
| Mold Temperature | 32.2 – 71.1 °C | 90.0 – 160 °F | Average value: 53.3 °C Grade Count:5 |