Ineos ABS Lustran® SMA 2171 SMA, Injection Molding Grade
| Manufacturer | Ineos ABS |
| Trade Name | Lustran® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Lustran® SMA 2171 is a high heat injection molding grade of impact-modified SMA (styrene/maleic anhydride) terpolymer offering an exceptional balance of processability and performance. Lustran® SMA 2171 has high heat resistance coupled with excellent chemical and impact resistance.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.07 g/cc | 1.07 g/cc | ASTM-D792 |
| Melt Flow | 6.0 g/10 min
@Load 10.0 kg,
Temperature 220 °C |
6.0 g/10 min
@Load 22.0 lb,
Temperature 428 °F |
ASTM-D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 98 | 98 | ASTM-D785 |
| Tensile Strength at Break | 29.1 MPa | 4220 psi | ASTM-D638 |
| 31.0 MPa | 4500 psi | ISO 527 | |
| Tensile Strength, Yield | 30.0 MPa | 4350 psi | ISO 527 |
| 31.3 MPa | 4540 psi | ASTM-D638 | |
| Tensile Modulus | 2.03 GPa | 295 ksi | ASTM-D638 |
| 2.05 GPa | 297 ksi | ISO 527 | |
| Flexural Yield Strength | 57.0 MPa | 8270 psi | ISO 178 |
| 93.1 MPa | 13500 psi | ASTM-D790 | |
| Flexural Modulus | 2.03 GPa | 294 ksi | ISO 178 |
| 2.07 GPa | 300 ksi | ASTM-D790 | |
| Izod Impact, Notched | 0.801 J/cm
@Thickness 3.17 mm,
Temperature -30.0 °C |
1.50 ft-lb/in
@Thickness 0.125 in,
Temperature -22.0 °F |
ASTM-D256 |
| 1.76 J/cm
@Thickness 3.17 mm,
Temperature 23.0 °C |
3.30 ft-lb/in
@Thickness 0.125 in,
Temperature 73.4 °F |
ASTM-D256 | |
| Izod Impact, Notched (ISO) | 7.30 kJ/m²
@Thickness 4.00 mm,
Temperature -30.0 °C |
3.47 ft-lb/in²
@Thickness 0.157 in,
Temperature -22.0 °F |
ISO 180/1A |
| 18.0 kJ/m²
@Thickness 4.00 mm,
Temperature 23.0 °C |
8.57 ft-lb/in²
@Thickness 0.157 in,
Temperature 73.4 °F |
ISO 180/1A | |
| Impact Test | 8.00 J
@Temperature -30.0 °C
|
5.90 ft-lb
@Temperature -22.0 °F
|
Multi-Axial Impact, Fractovis J; Energy Peak; ASTM-D3763 |
| 8.50 J
@Temperature -30.0 °C
|
6.27 ft-lb
@Temperature -22.0 °F
|
Multi-Axial Impact, Fractovis J; Energy Max; ASTM-D3763 | |
| 16.0 J
@Temperature 23.0 °C
|
11.8 ft-lb
@Temperature 73.4 °F
|
Multi-Axial Impact, Fractovis J; Energy Peak; ASTM-D3763 | |
| 20.0 J
@Temperature 23.0 °C
|
14.8 ft-lb
@Temperature 73.4 °F
|
Multi-Axial Impact, Fractovis J; Energy Max; ASTM-D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 105 °C
@Thickness 3.17 mm
|
221 °F
@Thickness 0.125 in
|
Unannealed; ASTM-D648 |
| 106 °C
@Thickness 4.00 mm
|
223 °F
@Thickness 0.157 in
|
Unannealed; ISO 75 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 90.0 °C
@Thickness 3.17 mm
|
194 °F
@Thickness 0.125 in
|
Unannealed; ASTM-D648 |
| 92.0 °C
@Thickness 4.00 mm
|
198 °F
@Thickness 0.157 in
|
Unannealed; ISO 75 | |
| Vicat Softening Point | 110 °C
@Load 5.00 kg
|
230 °F
@Load 11.0 lb
|
50°C/hour; ISO 306 |
| 127 °C
@Load 1.00 kg
|
261 °F
@Load 2.20 lb
|
120°C/hour; ASTM-D1525 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 240 – 255 °C | 464 – 491 °F | Injection Molding |
| Middle Barrel Temperature | 245 – 260 °C | 473 – 500 °F | Injection Molding |
| Front Barrel Temperature | 250 – 265 °C | 482 – 509 °F | Injection Molding |
| Nozzle Temperature | 250 – 265 °C | 482 – 509 °F | Injection Molding |
| Melt Temperature | 250 – 270 °C | 482 – 518 °F | Injection Molding |
| Mold Temperature | 60.0 – 85.0 °C | 140 – 185 °F | Injection Molding |
| Drying Temperature | 82.0 – 93.0 °C
@Time 7200 – 10800 sec
|
180 – 199 °F
@Time 2.00 – 3.00 hour
|
|
| Moisture Content | <= 0.10 % | <= 0.10 % | |
| Dew Point | <= -29.0 °C | <= -20.2 °F | inlet air |
| Back Pressure | 0.172 – 0.345 MPa | 25.0 – 50.0 psi | Injection Molding |
| Clamp Pressure | 30.8 – 61.6 MPa | 4470 – 8930 psi | Injection Molding |
| Cushion | <= 0.635 cm | <= 0.250 in | Injection Molding |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Injection Speed | Moderate | Injection Molding |
| Screw Compression Ratio | 2.5:1 | Injection Molding |
| Screw Length-to-Diameter Ratio | >= 20:1 | Injection Molding |
| Screw Speed | Moderate, Injection Molding | |
| Shot Weight-to-Machine Capacity Ratio | 0.5-0.75 | Injection Molding |