Sax Polymers SAXALEN PPH319FX21 Polypropylene Homopolymer
| Manufacturer | Sax Polymers |
| Trade Name | SAXALEN |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
SAXALEN PPH319FX21 is a unfilled Polypropylene – Homopolymer intended for injection molding. It has flame retardant properties and suitable to produce thin-walled parts.Information provided by SAX Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.910 g/cc | 0.0329 lb/in³ | |
| Melt Flow | 26 g/10 min
@Load 2.16 kg,
Temperature 230 °C |
26 g/10 min
@Load 4.76 lb,
Temperature 446 °F |
from MVR; ISO 1033 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 36.0 MPa | 5220 psi | 50 mm/min; ISO 527-1 |
| Elongation at Break | 6.0 % | 6.0 % | 50 mm/min; ISO 527-1 |
| Tensile Modulus | 2.10 GPa | 305 ksi | 1 mm/min; ISO 527-1 |
| Flexural Strength | 35.0 MPa | 5080 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 1.20 GPa | 174 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 2.00 kJ/m²
@Temperature -30.0 °C
|
0.952 ft-lb/in²
@Temperature -22.0 °F
|
ISO 180/1A |
| 4.00 kJ/m²
@Temperature 23.0 °C
|
1.90 ft-lb/in²
@Temperature 73.4 °F
|
ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 13.0 kJ/m²
@Temperature -30.0 °C
|
6.19 ft-lb/in²
@Temperature -22.0 °F
|
ISO 180/1U |
| 55.0 kJ/m²
@Temperature 23.0 °C
|
26.2 ft-lb/in²
@Temperature 73.4 °F
|
ISO 180/1U | |
| Charpy Impact Unnotched | 1.50 J/cm²
@Temperature -30.0 °C
|
7.14 ft-lb/in²
@Temperature -22.0 °F
|
ISO 179/1eU |
| 8.50 J/cm²
@Temperature 23.0 °C
|
40.4 ft-lb/in²
@Temperature 73.4 °F
|
ISO 179/1eU | |
| Charpy Impact, Notched | 0.200 J/cm²
@Temperature -30.0 °C
|
0.952 ft-lb/in²
@Temperature -22.0 °F
|
ISO 179/1eA |
| 0.400 J/cm²
@Temperature 23.0 °C
|
1.90 ft-lb/in²
@Temperature 73.4 °F
|
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 120 °C | 248 °F | 80*10*4 s=60mm; ISO 75-1 a |
| Flammability, UL94 | V-2 | V-2 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 210 – 240 °C | 410 – 464 °F | |
| Mold Temperature | 40.0 – 70.0 °C | 104 – 158 °F |