Tisan TISOPLEN® Flame Retardant (V0). Heat Stabilized, Copolymer Polypropylene
| Manufacturer | Tisan Engineering Plastics |
| Trade Name | TISOPLEN® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
TISOPLEN has a wide area of application in furniture, durable goods, household appliances, electrics/electronics, and telecommunication industries. General specifications include Low densityLow moisture intakeHigh impact resistanceExcellent chemical resistanceElectrical isolationHigh performance/affordable priceEasy processability Mineral filled TISOPLEN compounds have a long lasting thermal-dimensional stability, increased mechanical and hardness characteristics, decreased mold shrinkage and improved surface appearance. Glass fiber reinforcement will impart high tensile strength and impact resistance and yield improvements in thermal characteristics of TISOPLEN products. Excellent resistance to weak acids, weak alkalis, and strong alkalis. Good resistance to strong acids and alcohols. Medium resistance to hydrocarbons and engine fuels. Weak resistance to organic solvents.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.01 g/cc | 0.0365 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.017 cm/cm | 0.017 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 68 | 68 | ISO 868 |
| Tensile Strength at Break | 26.0 MPa | 3770 psi | ISO 527-2 |
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | ISO 527-2 |
| Elongation at Break | 40 % | 40 % | ISO 527-2 |
| Elongation at Yield | 39 % | 39 % | ISO 527-2 |
| Modulus of Elasticity | 1.50 GPa | 218 ksi | ISO 527-2 |
| Izod Impact, Notched (ISO) | 17.0 kJ/m² | 8.09 ft-lb/in² | ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 160 °C | 320 °F | |
| Vicat Softening Point | 150 °C | 302 °F | ISO 306 |
| Heat Distortion Temperature | 120 °C | 248 °F | ISO 75-2 |
| Flammability, UL94 | V-0 | V-0 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | 350 V | 350 V | TS EN 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 70.0 °C | 158 °F | |
| Rear Barrel Temperature | 190 – 210 °C | 374 – 410 °F | Aft-1. Region Temperature |
| Middle Barrel Temperature | 190 – 210 °C | 374 – 410 °F | Mid-2. Region Temperature |
| Front Barrel Temperature | 190 – 210 °C | 374 – 410 °F | Pre-3. Region Temperature |
| Nozzle Temperature | 200 °C | 392 °F | |
| Melt Temperature | 170 – 190 °C | 338 – 374 °F | |
| Drying Temperature | 80.0 °C | 176 °F | Predrying Temperature |
| Dry Time | 1 hour | 1 hour | Predrying Time |
| Moisture Content | 0.20 % | 0.20 % | ISO 62 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Block Temperature | 45°C |