A. Schulman POLYFLAM™ RPP 1174 Talc Filled, Homopolymer Polypropylene
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
DescriptionPolyflam® RPP 1174 is a high performance talc filled homopolymer polypropylene product with UL V0 flammability and 105°C temperature index at 0.81 mm. RPP 1174 is non-dripping and has excellent dimensional stability.Information provided by A. Schulman.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.38 g/cc | 1.38 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0090 – 0.012 cm/cm | 0.0090 – 0.012 in/in | ASTM D955 |
| Melt Flow | 8.0 g/10 min | 8.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 22.0 MPa | 3190 psi | ASTM D638 |
| Elongation at Break | 45 % | 45 % | ASTM D638 |
| Flexural Modulus | 2.00 GPa | 290 ksi | ASTM D790 |
| Izod Impact, Notched | 0.270 J/cm | 0.506 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 116 °C | 241 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 69.0 °C | 156 °F | ASTM D648 |
| UL RTI, Electrical | 105 °C | 221 °F | 0.030 inch sample |
| Flammability, UL94 | V-0
@Thickness 0.810 mm
|
V-0
@Thickness 0.0319 in
|
|
| V-0
@Thickness 1.57 mm
|
V-0
@Thickness 0.0618 in
|
||
| V-0
@Thickness 3.05 mm
|
V-0
@Thickness 0.120 in
|