Addiplast Addilene PMD 50271 Flame Retardant Polypropylene
| Manufacturer | Addiplast |
| Trade Name | Addilene |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Flame retardant, high rigidityInformation provided by Addiplast.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.38 g/cc | 0.0499 lb/in³ | ISO 1183/A |
| Melt Flow | 16 g/10 min | 16 g/10 min | ISO 1133 |
Thermoplastic
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 80 | 80 | Conditioned; ISO 868 |
| Tensile Strength at Break | 70.0 MPa | 10200 psi | Conditioned; ISO R 527 |
| Elongation at Break | 4.0 % | 4.0 % | Conditioned; ISO R 527 |
| Modulus of Elasticity | 7.00 GPa | 1020 ksi | Conditioned; ISO 178 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | Conditioned; ISO 180/1A |
| Charpy Impact Unnotched | 1.80 J/cm² | 8.57 ft-lb/in² | Conditioned; ISO 179/IeU |
| Charpy Impact, Notched | 0.550 J/cm² | 2.62 ft-lb/in² | Conditioned; ISO 179/IeA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 165 – 168 °C | 329 – 334 °F | ISO 3146/C2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 146 °C | 295 °F | ISO 75-2/AF |
| Vicat Softening Point | 163 °C | 325 °F | ISO 306/A50 |
| Flammability, UL94 | V-2
@Thickness 1.60 mm
|
V-2
@Thickness 0.0630 in
|
|
| Oxygen Index | 23 % | 23 % | ISO 4589 |
| Glow Wire Test | 750 °C | 1380 °F | CEI 60695/2/1 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | Conditioned; CEI 60093 |
| Surface Resistance | >= 1.00e+13 ohm | >= 1.00e+13 ohm | Conditioned; CEI 60093 |
| Comparative Tracking Index | >= 600 V | >= 600 V | CEI 60112/Solution A |