Diamond Polymers SAN 280 Styrene Acrylonitrile, Transparent Engineering Thermoplastic
| Manufacturer | Diamond and Network Polymers |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.07 g/cc | 1.07 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0030 – 0.0070 cm/cm | 0.0030 – 0.0070 in/in | ASTM D955 |
| Melt Flow | 4.0 g/10 min
@Load 5.00 kg,
Temperature 200 °C |
4.0 g/10 min
@Load 11.0 lb,
Temperature 392 °F |
ASTM D1238 |
| 14.3 g/10 min
@Load 3.80 kg,
Temperature 230 °C |
14.3 g/10 min
@Load 8.38 lb,
Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 122 | 122 | ASTM D785 |
| Tensile Strength, Yield | 63.7 MPa | 9240 psi | chs 2.0 in/min; ASTM D638 |
| Flexural Modulus | 3.43 GPa | 497 ksi | chs 0.05 in/min; tangent; ASTM D790 |
| Izod Impact, Notched | 0.160 J/cm
@Thickness 3.17 mm,
Temperature 23.0 °C |
0.300 ft-lb/in
@Thickness 0.125 in,
Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 106 °C
@Load 1.00 kg,
Thickness 3.17 mm |
223 °F
@Load 2.20 lb,
Thickness 0.125 in |
ASTM D1525 |
| Flammability, UL94 | HB
@Thickness 1.59 mm
|
HB
@Thickness 0.0625 in
|
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 1.1 % | 1.1 % | ASTM D1003 |
| Transmission, Visible | 90.5 % | 90.5 % | ASTM D1003 |