Polykemi AB POLYfill PP CQX30030 RTX Polypropylene, Mineral Reinforced, Scratch Resistant
| Manufacturer | Polykemi AB |
| Trade Name | POLYfill |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Information provided by Polykemi AB
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ISO 1183 |
| Filler Content | 30 % | 30 % | ±2%; Polykemi |
| Linear Mold Shrinkage | 0.012 – 0.014 cm/cm | 0.012 – 0.014 in/in | With Flow; ISO 2577 |
| 0.012 – 0.014 cm/cm | 0.012 – 0.014 in/in | Across Flow; ISO 2577 | |
| Melt Index of Compound | 30 g/10 min
@Load 2.16 kg,
Temperature 230 °C |
30 g/10 min
@Load 4.76 lb,
Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | <= 19.0 MPa | <= 2760 psi | ISO/R527 |
| Elongation at Break | 36 % | 36 % | ISO/R527 |
| Elongation at Yield | 8.0 % | 8.0 % | ISO/R527 |
| Flexural Strength | <= 37.0 MPa | <= 5370 psi | ISO 178 |
| Flexural Modulus | 1.90 GPa
@Temperature 23.0 °C
|
276 ksi
@Temperature 73.4 °F
|
ISO 178 |
| Charpy Impact Unnotched | 2.10 J/cm²
@Temperature -20.0 °C
|
9.99 ft-lb/in²
@Temperature -4.00 °F
|
ISO 179 |
| 3.60 J/cm²
@Temperature 23.0 °C
|
17.1 ft-lb/in²
@Temperature 73.4 °F
|
ISO 179 | |
| Charpy Impact, Notched | 0.300 J/cm²
@Temperature -20.0 °C
|
1.43 ft-lb/in²
@Temperature -4.00 °F
|
ISO 179 |
| 0.400 J/cm²
@Temperature 23.0 °C
|
1.90 ft-lb/in²
@Temperature 73.4 °F
|
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 70.0 – 90.0 µm/m-°C | 38.9 – 50.0 µin/in-°F | Polykemi |
| Deflection Temperature at 0.46 MPa (66 psi) | 110 °C | 230 °F | 120°C/h; ISO 75/1 |
| Deflection Temperature at 1.8 MPa (264 psi) | 58.0 °C | 136 °F | 120°C/h; ISO 75/1 |
| Vicat Softening Point | 75.0 °C
@Load 5.001 kg
|
167 °F
@Load 11.03 lb
|
50°C/h; ISO 306 |
| 148 °C
@Load 1.00 kg
|
298 °F
@Load 2.21 lb
|
50°C/h; ISO 306 | |
| Flammability, UL94 | HB
@Thickness 1.60 mm
|
HB
@Thickness 0.0630 in
|
|
| Glow Wire Test | 750 °C
@Thickness 2.00 mm
|
1380 °F
@Thickness 0.0787 in
|
IEC 695-2-1 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 230 – 250 °C | 446 – 482 °F | |
| Mold Temperature | 40.0 – 60.0 °C | 104 – 140 °F | |
| Drying Temperature | 70.0 – 80.0 °C | 158 – 176 °F | |
| Dry Time | 2 – 4 hour | 2 – 4 hour | in circulation dryer |
| 2 – 4 hour | 2 – 4 hour | in desiccant air dryer | |
| Injection Pressure | 40.0 – 70.0 MPa | 5800 – 10200 psi | |
| Back Pressure | 1.00 – 1.50 MPa | 145 – 218 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Holding Pressure () | > 40 | % of injection pressure |
| Injection Speed () | High | |
| Scratch Resistance, 10N (dL) | < 0.1 | 10N Fine Structure; ISO 1518/D65 |