| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Noryl* GFN1420V resin is a high flow blend of polyphenylene ether (PPE) and polystyrene (PS) resin that contains 20 % glass reinforcement. The resin is suitable for injection molding and is designed to have higher flow compared to Noryl GFN1520V resin. Noryl GFN1420V resin will be certified for potable water applications up to 85C in Europe and North America in limited colors.This data was supplied by SABIC-IP for the Asia Pacific region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.24 g/cc | 1.24 g/cc | ASTM D 792 |
| Density | 1.24 g/cc | 0.0448 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.060 % | 0.060 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.20 %
@Temperature 23.0 °C
|
0.20 %
@Temperature 73.4 °F
|
ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0020 – 0.0040 cm/cm
@Thickness 3.20 mm
|
0.0020 – 0.0040 in/in
@Thickness 0.126 in
|
SABIC Method |
| Melt Flow | 11 g/10 min
@Load 5.00 kg,
Temperature 280 °C |
11 g/10 min
@Load 11.0 lb,
Temperature 536 °F |
ASTM D 1238 |
| 23 g/10 min
@Load 10.0 kg,
Temperature 280 °C |
23 g/10 min
@Load 22.0 lb,
Temperature 536 °F |
[cm^3/10 min] Melt Volume Rate; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 105 MPa | 15200 psi | 5 mm/min; ISO 527 |
| 109 MPa | 15800 psi | Type I, 5 mm/min; ASTM D 638 | |
| Tensile Strength, Yield | 105 MPa | 15200 psi | 5 mm/min; ISO 527 |
| 109 MPa | 15800 psi | Type I, 5 mm/min; ASTM D 638 | |
| Elongation at Break | 2.5 % | 2.5 % | Type I, 5 mm/min; ASTM D 638 |
| 2.5 % | 2.5 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 2.5 % | 2.5 % | Type I, 5 mm/min; ASTM D 638 |
| 2.5 % | 2.5 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 6.40 GPa | 928 ksi | 1 mm/min; ISO 527 |
| 6.50 GPa | 943 ksi | 5 mm/min; ASTM D 638 | |
| Flexural Yield Strength | 155 MPa | 22500 psi | 2 mm/min; ISO 178 |
| 159 MPa | 23100 psi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Flexural Modulus | 5.80 GPa | 841 ksi | 2 mm/min; ISO 178 |
| 5.90 GPa | 856 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Izod Impact, Notched | 0.920 J/cm
@Temperature -30.0 °C
|
1.72 ft-lb/in
@Temperature -22.0 °F
|
ASTM D 256 |
| 0.980 J/cm
@Temperature 23.0 °C
|
1.84 ft-lb/in
@Temperature 73.4 °F
|
ASTM D 256 | |
| Izod Impact, Unnotched | 5.10 J/cm
@Temperature 23.0 °C
|
9.55 ft-lb/in
@Temperature 73.4 °F
|
ASTM D 4812 |
| 5.10 J/cm
@Temperature -30.0 °C
|
9.55 ft-lb/in
@Temperature -22.0 °F
|
ASTM D 4812 | |
| Izod Impact, Unnotched (ISO) | 30.0 kJ/m²
@Temperature 23.0 °C
|
14.3 ft-lb/in²
@Temperature 73.4 °F
|
80*10*4; ISO 180/1U |
| 30.0 kJ/m²
@Temperature -30.0 °C
|
14.3 ft-lb/in²
@Temperature -22.0 °F
|
80*10*4; ISO 180/1U | |
| Charpy Impact Unnotched | 3.00 J/cm²
@Temperature 23.0 °C
|
14.3 ft-lb/in²
@Temperature 73.4 °F
|
Edgew 80*10*4 sp=62mm; ISO 179/1eU |
| 3.00 J/cm²
@Temperature -30.0 °C
|
14.3 ft-lb/in²
@Temperature -22.0 °F
|
Edgew 80*10*4 sp=62mm; ISO 179/1eU | |
| Impact Test | 17.0 J
@Temperature 23.0 °C
|
12.5 ft-lb
@Temperature 73.4 °F
|
Instrumented Impact Total Energy; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 30.0 µm/m-°C
@Temperature -40.0 – 40.0 °C
|
16.7 µin/in-°F
@Temperature -40.0 – 104 °F
|
ASTM E 831 |
| 30.0 µm/m-°C
@Temperature -40.0 – 40.0 °C
|
16.7 µin/in-°F
@Temperature -40.0 – 104 °F
|
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 70.0 µm/m-°C
@Temperature -40.0 – 40.0 °C
|
38.9 µin/in-°F
@Temperature -40.0 – 104 °F
|
ASTM E 831 |
| 70.0 µm/m-°C
@Temperature -40.0 – 40.0 °C
|
38.9 µin/in-°F
@Temperature -40.0 – 104 °F
|
ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 131 °C | 268 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 132 °C
@Thickness 3.20 mm
|
270 °F
@Thickness 0.126 in
|
unannealed; ASTM D 648 | |
| Vicat Softening Point | 135 °C | 275 °F | Rate B/50; ASTM D 1525 |
| 135 °C | 275 °F | Rate B/50; ISO 306 | |
| 141 °C | 286 °F | Rate B/120; ISO 306 |