A. Schulman POLYFLAM™ E-15937B High Strength Impact Modified Polypropylene
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
DescriptionPolyfort® E-15937B is a high strength impact modified polypropylene.Information provided by A. Schulman.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.09 g/cc | 1.09 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.013 cm/cm | 0.013 in/in | ASTM D955 |
| Melt Flow | 3.0 – 11 g/10 min
@Load 2.16 kg,
Temperature 230 °C |
3.0 – 11 g/10 min
@Load 4.76 lb,
Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 31.0 MPa | 4500 psi | ASTM D638 |
| Elongation at Break | 23 % | 23 % | ASTM D638 |
| Flexural Strength | 48.0 MPa | 6960 psi | ASTM D790 |
| Flexural Modulus | 2.892 GPa | 419.5 ksi | ASTM D790 |
| Izod Impact, Notched | 0.530 J/cm | 0.993 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.29 J/cm | 9.91 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 112 °C | 234 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | ASTM D648 |
| DSC Induction Temperature | 165 °C | 329 °F | at 10aC/min; ASTM D3418 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Flammability | SE | FMVSS 302 |
| Surface Resistivity | 89 | R-Scale (ASTM D785) |