A. Schulman POLYFORT™ FPP 1182E Talc Filled, Extrusion Grade Copolymer Polypropylene
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
DescriptionPolyfort® FPP 1182E is a 20% talc-filled, extrusion grade copolymer polypropylene. It had a good balance of flexural modulus, low temperature impact, and appearance properties. Information provided by A. Schulman.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.04 g/cc | 1.04 g/cc | ASTM D792 |
| Melt Flow | 0.90 g/10 min
@Temperature 230 °C
|
0.90 g/10 min
@Temperature 446 °F
|
Condition L; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 90 | 90 | ASTM D785 |
| Tensile Strength at Break | 18.0 MPa | 2610 psi | ISO 527 |
| Tensile Strength, Yield | 27.6 MPa | 4000 psi | 2 in/min; ASTM D638 |
| Elongation at Yield | 30 % | 30 % | ASTM D638 |
| Flexural Modulus | 1.45 GPa | 210 ksi | ASTM D790 |
| Izod Impact, Notched | 3.20 J/cm | 6.00 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | NB | NB | -22°F; ASTM D256 |
| Gardner Impact | 14.47 J | 10.67 ft-lb | ASTM D3029 |
| 43.4 J
@Temperature -28.9 °C
|
32.0 ft-lb
@Temperature -20.0 °F
|
ASTM D3029 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 113 °C | 235 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 °C | 122 °F | ISO 75 |
| 62.8 °C | 145 °F | ASTM D648 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Thermal Oxidative Stability | Pass | ASTM D3012, at 336 hrs, 150°C |