Addiplast Addilene J 490 S Flame Retardant Polypropylene
| Manufacturer | Addiplast |
| Trade Name | Addilene |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Flame retardant, unreinforced, with halogensInformation provided by Addiplast.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.940 g/cc | 0.0340 lb/in³ | ISO 1183/A |
| Melt Flow | 12 g/10 min | 12 g/10 min | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 65 | 65 | Conditioned; ISO 868 |
| Tensile Strength at Break | 26.0 MPa | 3770 psi | Conditioned; ISO R 527 |
| Elongation at Break | >= 100 % | >= 100 % | Conditioned; ISO R 527 |
| Modulus of Elasticity | 1.00 GPa | 145 ksi | Conditioned; ISO 178 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | Conditioned; ISO 180/1A |
| Charpy Impact Unnotched | NB | NB | Conditioned; ISO 179/IeU |
| Charpy Impact, Notched | 1.00 J/cm² | 4.76 ft-lb/in² | Conditioned; ISO 179/IeA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 165 – 168 °C | 329 – 334 °F | ISO 3146/C2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 51.0 °C | 124 °F | ISO 75-2/AF |
| Vicat Softening Point | 152 °C | 306 °F | ISO 306/A50 |
| Flammability, UL94 | V-2
@Thickness 1.60 mm
|
V-2
@Thickness 0.0630 in
|
|
| Oxygen Index | 26 % | 26 % | ISO 4589 |
| Glow Wire Test | 960 °C | 1760 °F | CEI 60695/2/1 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | Conditioned; CEI 60093 |
| Surface Resistance | >= 1.00e+13 ohm | >= 1.00e+13 ohm | Conditioned; CEI 60093 |
| Dielectric Strength | 43.0 kV/mm | 1090 kV/in | CEI 60243-1 |
| Comparative Tracking Index | >= 600 V | >= 600 V | CEI 60112/Solution A |