Arkema Group Appryl® CZU 0525 Polypropylene, 25% Talc Filled
| Manufacturer | Arkema |
| Trade Name | Appryl® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Compound of a PP copolymer modified with EPR and 25% talc. This grade has been specially developed for exterior trim automotive applications, that required an excellent impact test associated with a high modulus.It is UV stabilized and has a good paintability.Main application is side panels.ISO data provided by the manufacturer, Arkema.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.12 g/cc | 0.0405 lb/in³ | |
| Melt Flow | 7.0 g/10 min
@Load 2.16 kg,
Temperature 230 °C |
7.0 g/10 min
@Load 4.76 lb,
Temperature 446 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 19.0 MPa | 2760 psi | 50 mm/min |
| Elongation at Break | 26 % | 26 % | Nominal Strain; 50 mm/min |
| Elongation at Yield | 4.0 % | 4.0 % | 50 mm/min |
| Tensile Modulus | 1.92 GPa | 278 ksi | 1 mm/min |
| Charpy Impact Unnotched | NB | NB | |
| Charpy Impact, Notched | 1.30 J/cm² | 6.19 ft-lb/in² | |
| 0.360 J/cm²
@Temperature -30.0 °C
|
1.71 ft-lb/in²
@Temperature -22.0 °F
|
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 161 °C | 322 °F | 10°C/min |
| Deflection Temperature at 0.46 MPa (66 psi) | 102 °C | 216 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 58.0 °C | 136 °F | |
| Vicat Softening Point | 52.0 °C | 126 °F | 50°C/hr; 50N |