Asahi Kasei Thermylene® P-30FG-0812 30% Glass Fiber Reinforced, UV Stabilized
| Manufacturer | Asahi Kasei |
| Trade Name | Thermylene® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Information provided by Asahi Thermofil
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.13 g/cc | 1.13 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | ASTM D955 |
| Melt Flow | 2.0 g/10 min | 2.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 93 | 93 | ASTM D785 |
| Tensile Strength, Yield | 72.4 MPa | 10500 psi | ASTM D638 |
| Elongation at Yield | 3.0 % | 3.0 % | ASTM D638 |
| Tensile Modulus | 4.83 GPa | 700 ksi | ASTM D638 |
| Flexural Strength | 89.6 MPa | 13000 psi | ASTM D790 |
| Flexural Modulus | 5.03 GPa | 730 ksi | ASTM D790 |
| Izod Impact, Notched | 0.481 J/cm | 0.900 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 1.60 J/cm | 3.00 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 37.8 µm/m-°C
@Temperature 20.0 °C
|
21.0 µin/in-°F
@Temperature 68.0 °F
|
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 154 °C | 310 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 149 °C | 300 °F | ASTM D648 |
| Flammability, UL94 | HB | HB | 0.0591 in thickness |