BASF Ultrason S 2010 G6 30% Glass Filled PSU
| Manufacturer | BASF |
| Trade Name | Ultrason S |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Ultrason S 2010 G6 is a 30% glass reinforced, medium viscosity injection molding PSU grade with high rigidity and strength.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.49 g/cc | 0.0538 lb/in³ | ISO 1183 |
| Water Absorption | 0.60 % | 0.60 % | ISO 62 |
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | 23°C/50% R.H.; ISO 62 |
| Viscosity Test | 63 cm³/g | 63 cm³/g | Viscosity number |
| Linear Mold Shrinkage, Flow | 0.0029 cm/cm | 0.0029 in/in | ISO 294 |
| Linear Mold Shrinkage, Transverse | 0.0046 cm/cm | 0.0046 in/in | ISO 294 |
| Melt Flow | 30 g/10 min
@Load 10.0 kg,
Temperature 360 °C |
30 g/10 min
@Load 22.0 lb,
Temperature 680 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 193 MPa | 28000 psi | ISO 2039-1 |
| Tensile Strength at Break | 120 MPa | 17400 psi | 5mm/min; ISO 527-2 |
| 52.0 MPa
@Temperature 160 °C
|
7540 psi
@Temperature 320 °F
|
||
| 80.0 MPa
@Temperature 120 °C
|
11600 psi
@Temperature 248 °F
|
||
| 120 MPa
@Temperature 40.0 °C
|
17400 psi
@Temperature 104 °F
|
||
| 125 MPa
@Temperature 0.000 °C
|
18100 psi
@Temperature 32.0 °F
|
||
| Tensile Stress | 50.0 MPa
@Strain 0.600 %,
Temperature 23.0 °C |
7250 psi
@Strain 0.600 %,
Temperature 73.4 °F |
|
| 50.0 MPa
@Strain 1.70 %,
Temperature 160 °C |
7250 psi
@Strain 1.70 %,
Temperature 320 °F |
||
| 55.0 MPa
@Strain 1.00 %,
Temperature 160 °C |
7980 psi
@Strain 1.00 %,
Temperature 320 °F |
||
| 80.0 MPa
@Strain 1.00 %,
Temperature 23.0 °C |
11600 psi
@Strain 1.00 %,
Temperature 73.4 °F |
||
| 105 MPa
@Strain 1.50 %,
Temperature 23.0 °C |
15200 psi
@Strain 1.50 %,
Temperature 73.4 °F |
||
| Tensile Strength, Yield | 120 MPa | 17400 psi | 50mm/min; ISO 527-2 |
| Elongation at Break | 1.7 % | 1.7 % | 5mm/min; ISO 527-2 |
| Elongation at Yield | 1.7 % | 1.7 % | 50mm/min; ISO 527-2 |
| 0.20 %
@Time 3600 sec,
Pressure 10.0 MPa |
0.20 %
@Time 1.00 hour,
Pressure 1450 psi |
140°C; ISO 899 | |
| 0.20 %
@Time 3600 sec,
Pressure 15.0 MPa |
0.20 %
@Time 1.00 hour,
Pressure 2180 psi |
ISO 899 | |
| 0.20 %
@Pressure 15.0 MPa,
Time 360000 sec |
0.20 %
@Pressure 2180 psi,
Time 100 hour |
ISO 899 | |
| 0.20 %
@Pressure 15.0 MPa,
Time 3.60e+7 sec |
0.20 %
@Pressure 2180 psi,
Time 10000 hour |
ISO 899 | |
| 0.25 %
@Pressure 10.0 MPa,
Time 360000 sec |
0.25 %
@Pressure 1450 psi,
Time 100 hour |
140°C; ISO 899 | |
| 0.30 %
@Pressure 10.0 MPa,
Time 3.60e+7 sec |
0.30 %
@Pressure 1450 psi,
Time 10000 hour |
140°C; ISO 899 | |
| 0.30 %
@Time 3600 sec,
Pressure 20.0 MPa |
0.30 %
@Time 1.00 hour,
Pressure 2900 psi |
140°C; ISO 899 | |
| 0.35 %
@Pressure 20.0 MPa,
Time 360000 sec |
0.35 %
@Pressure 2900 psi,
Time 100 hour |
140°C; ISO 899 | |
| 0.39 %
@Time 3600 sec,
Pressure 30.0 MPa |
0.39 %
@Time 1.00 hour,
Pressure 4350 psi |
ISO 899 | |
| 0.40 %
@Time 3600 sec,
Pressure 30.0 MPa |
0.40 %
@Time 1.00 hour,
Pressure 4350 psi |
140°C; ISO 899 | |
| 0.40 %
@Pressure 30.0 MPa,
Time 360000 sec |
0.40 %
@Pressure 4350 psi,
Time 100 hour |
ISO 899 | |
| 0.41 %
@Pressure 30.0 MPa,
Time 3.60e+7 sec |
0.41 %
@Pressure 4350 psi,
Time 10000 hour |
ISO 899 | |
| 0.50 %
@Pressure 20.0 MPa,
Time 3.60e+7 sec |
0.50 %
@Pressure 2900 psi,
Time 10000 hour |
140°C; ISO 899 | |
| 0.50 %
@Pressure 30.0 MPa,
Time 360000 sec |
0.50 %
@Pressure 4350 psi,
Time 100 hour |
140°C; ISO 899 | |
| 0.50 %
@Time 3600 sec,
Pressure 40.0 MPa |
0.50 %
@Time 1.00 hour,
Pressure 5800 psi |
140°C; ISO 899 | |
| 0.55 %
@Pressure 40.0 MPa,
Time 360000 sec |
0.55 %
@Pressure 5800 psi,
Time 100 hour |
140°C; ISO 899 | |
| 0.59 %
@Time 3600 sec,
Pressure 45.0 MPa |
0.59 %
@Time 1.00 hour,
Pressure 6530 psi |
ISO 899 | |
| 0.60 %
@Pressure 45.0 MPa,
Time 360000 sec |
0.60 %
@Pressure 6530 psi,
Time 100 hour |
ISO 899 | |
| 0.60 %
@Time 3600 sec,
Pressure 45.0 MPa |
0.60 %
@Time 1.00 hour,
Pressure 6530 psi |
140°C; ISO 899 | |
| 0.61 %
@Pressure 45.0 MPa,
Time 3.60e+7 sec |
0.61 %
@Pressure 6530 psi,
Time 10000 hour |
ISO 899 | |
| 0.80 %
@Time 3600 sec,
Pressure 60.0 MPa |
0.80 %
@Time 1.00 hour,
Pressure 8700 psi |
ISO 899 | |
| 0.82 %
@Pressure 60.0 MPa,
Time 360000 sec |
0.82 %
@Pressure 8700 psi,
Time 100 hour |
ISO 899 | |
| 0.90 %
@Pressure 60.0 MPa,
Time 3.60e+7 sec |
0.90 %
@Pressure 8700 psi,
Time 10000 hour |
ISO 899 | |
| 0.90 %
@Pressure 30.0 MPa,
Time 3.60e+7 sec |
0.90 %
@Pressure 4350 psi,
Time 10000 hour |
140°C; ISO 899 | |
| 1.2 %
@Time 3600 sec,
Pressure 80.0 MPa |
1.2 %
@Time 1.00 hour,
Pressure 11600 psi |
ISO 899 | |
| 1.35 %
@Pressure 80.0 MPa,
Time 360000 sec |
1.35 %
@Pressure 11600 psi,
Time 100 hour |
ISO 899 | |
| 1.4 %
@Pressure 40.0 MPa,
Time 3.60e+7 sec |
1.4 %
@Pressure 5800 psi,
Time 10000 hour |
140°C; ISO 899 | |
| 1.55 %
@Pressure 80.0 MPa,
Time 3.60e+7 sec |
1.55 %
@Pressure 11600 psi,
Time 10000 hour |
ISO 899 | |
| 1.6 %
@Pressure 45.0 MPa,
Time 3.60e+7 sec |
1.6 %
@Pressure 6530 psi,
Time 10000 hour |
140°C; ISO 899 | |
| 1.9 %
@Pressure 45.0 MPa,
Time 360000 sec |
1.9 %
@Pressure 6530 psi,
Time 100 hour |
140°C; ISO 899 | |
| Creep Strength | 23.0 MPa
@Time 3.60e+7 sec
|
3340 psi
@Time 10000 hour
|
in water at 95°C |
| 30.0 MPa
@Time 3.60e+6 sec
|
4350 psi
@Time 1000 hour
|
in water at 95°C | |
| 40.0 MPa
@Time 360000 sec
|
5800 psi
@Time 100 hour
|
in water at 95°C | |
| 51.0 MPa
@Time 36000 sec
|
7400 psi
@Time 10.0 hour
|
in water at 95°C | |
| Modulus of Elasticity | 7.50 GPa
@Temperature 160 °C
|
1090 ksi
@Temperature 320 °F
|
ISO 527 |
| 8.70 GPa
@Temperature 80.0 °C
|
1260 ksi
@Temperature 176 °F
|
ISO 527 | |
| 8.80 GPa
@Temperature 60.0 °C
|
1280 ksi
@Temperature 140 °F
|
ISO 527 | |
| 9.00 GPa
@Temperature 120 °C
|
1310 ksi
@Temperature 248 °F
|
ISO 527 | |
| 9.00 GPa
@Temperature 20.0 °C
|
1310 ksi
@Temperature 68.0 °F
|
ISO 527 | |
| Tensile Modulus | 8.30 GPa | 1200 ksi | Elasticity; ISO 527-1/-2 |
| Fatigue Strength | 45.0 MPa
@# of Cycles 1.00e+6
|
6530 psi
@# of Cycles 1.00e+6
|
|
| 55.0 MPa
@# of Cycles 100000
|
7980 psi
@# of Cycles 100000
|
||
| 69.0 MPa
@# of Cycles 10000
|
10000 psi
@# of Cycles 10000
|
||
| Shear Modulus | 0.0250 GPa
@Temperature 200 °C
|
3.63 ksi
@Temperature 392 °F
|
ISO 6721 |
| 0.800 GPa
@Temperature 175 °C
|
116 ksi
@Temperature 347 °F
|
ISO 6721 | |
| 0.900 GPa
@Temperature 100 °C
|
131 ksi
@Temperature 212 °F
|
ISO 6721 | |
| 0.950 GPa
@Temperature 50.0 °C
|
138 ksi
@Temperature 122 °F
|
ISO 6721 | |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² | 3.33 ft-lb/in² | ISO 180/A |
| 7.00 kJ/m²
@Temperature -30.0 °C
|
3.33 ft-lb/in²
@Temperature -22.0 °F
|
ISO 180/A | |
| Izod Impact, Unnotched (ISO) | 36.0 kJ/m²
@Temperature 120 °C
|
17.1 ft-lb/in²
@Temperature 248 °F
|
ISO 179/1eU |
| 37.0 kJ/m²
@Temperature 70.0 °C
|
17.6 ft-lb/in²
@Temperature 158 °F
|
ISO 179/1eU | |
| 41.0 kJ/m²
@Temperature 25.0 °C
|
19.5 ft-lb/in²
@Temperature 77.0 °F
|
ISO 179/1eU | |
| 42.0 kJ/m²
@Temperature 0.000 °C
|
20.0 ft-lb/in²
@Temperature 32.0 °F
|
ISO 179/1eU | |
| 50.0 kJ/m²
@Temperature -25.0 °C
|
23.8 ft-lb/in²
@Temperature -13.0 °F
|
ISO 179/1eU | |
| Charpy Impact Unnotched | 4.00 J/cm² | 19.0 ft-lb/in² | ISO 179/1eU |
| 4.00 J/cm²
@Temperature -30.0 °C
|
19.0 ft-lb/in²
@Temperature -22.0 °F
|
ISO 179/1eU |