Bond Laminates TEPEX® dynalite 104-RG600(x)/47% Roving Glass – PP Consolidated Composite Laminate
| Manufacturer | Bond Laminates |
| Trade Name | TEPEX® dynalite |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Within the TEPEX® composite laminate, PP is a resin known for its good hardness, stiffness, abrasion resistance and chemical resistance.Typical application environments are within automotive applications, large structural parts.Information provided by Bond Laminates, GmbH.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.68 g/cc | 0.0607 lb/in³ | |
| Filler Content | 47 % | 47 % | by volume |
| Thickness | 500 microns | 19.7 mil | laminate layer thickness |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 390 MPa | 56600 psi | transverse; ISO 527-4/5 |
| 400 MPa | 58000 psi | longitudinal; ISO 527-4/5 | |
| Tensile Modulus | 20.1 GPa | 2920 ksi | transverse; ISO 527-4/5 |
| 20.5 GPa | 2970 ksi | longitudinal; ISO 527-4/5 | |
| Flexural Strength | 365 MPa | 52900 psi | transverse; ISO 178 |
| 370 MPa | 53700 psi | longitudinal; ISO 178 | |
| Flexural Modulus | 17.0 GPa | 2470 ksi | transverse; ISO 178 |
| 17.5 GPa | 2540 ksi | longitudinal; ISO 178 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 163 °C | 325 °F | DSC 3146 |
| Maximum Service Temperature, Air | 90.0 °C
@Time 7.20e+7 sec
|
194 °F
@Time 20000 hour
|
Relative Temperature Index; IEC 216/1 |
| Deflection Temperature at 1.8 MPa (264 psi) | 158 °C | 316 °F | ISO 75-1/2 |
| Minimum Service Temperature, Air | -10.0 °C | 14.0 °F |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 190 – 210 °C | 374 – 410 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Reinforcement | Area weight | 600 g/m² |
| Fabric | twill 2/2 | |
| Fibers | roving glass | |
| Weight Rate | 50% longitudinal and transverse | |
| Yarn | 1200 tex longitudinal and transverse |