Carmel Olefins CAPILENE® G 70 TF Polypropylene Homopolymer
| Manufacturer | Carmel Olefins |
| Trade Name | CAPILENE® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Description: CAPILENE® G 70 TF is a nucleated polypropylene homopolymer intended for sheet extrusion and thermoforming applications. This grade exhibits high stiffness, high gloss, good contact transparency, short cycle time and improved characteristics at high temperature.Applications: CAPILENE® G 70 TF is suitable for extrusion-thermoforming of thin, stiff and transparent food containers, containers for higher temperature filling.Information provided by Carmel Olefins.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Flow | 3.0 g/10 min
@Load 2.16 kg,
Temperature 230 °C |
3.0 g/10 min
@Load 4.76 lb,
Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 38.0 MPa | 5510 psi | 50 mm/min; ASTM D638 |
| Elongation at Yield | 9.0 % | 9.0 % | 50 mm/min; ASTM D638 |
| Flexural Modulus | 2.10 GPa | 305 ksi | ASTM D790 |
| Izod Impact, Notched | 0.300 J/cm | 0.562 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 122 °C | 252 °F | ASTM D648 |
| Vicat Softening Point | 159 °C
@Load 1.02 kg
|
318 °F
@Load 2.25 lb
|
ASTM D1525 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 30 %
@Thickness 1.00 mm
|
30 %
@Thickness 0.0394 in
|
ASTM D1003 |
| Transmission, Visible | 90 % | 90 % | transparent; thickness not quantified |