Cossa Polimeri ESTAPROP H 0560 GFCTG Polypropylene, 30% Mixed Filler
| Manufacturer | Cossa Polimeri S.r.L. |
| Trade Name | ESTAPROP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
PP homopolymer 30% mixed fillerGood physical and mechanical characteristicsInformation provided by Cossa Polimeri S.r.l.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ASTM D 792 |
| Linear Mold Shrinkage | 0.0060 – 0.0080 cm/cm | 0.0060 – 0.0080 in/in | ASTM D 955 |
| Melt Flow | 8.0 g/10 min
@Load 2.16 kg,
Temperature 230 °C |
8.0 g/10 min
@Load 4.76 lb,
Temperature 446 °F |
ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 50.0 MPa | 7250 psi | ASTM D 638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D 638 |
| Tensile Modulus | 4.70 GPa | 682 ksi | ASTM D 638 |
| Flexural Modulus | 4.30 GPa | 624 ksi | ASTM D 790 |
| Izod Impact, Notched | 0.350 J/cm
@Temperature -20.0 °C
|
0.656 ft-lb/in
@Temperature -4.00 °F
|
ASTM D 638 |
| 0.500 J/cm
@Temperature 0.000 °C
|
0.937 ft-lb/in
@Temperature 32.0 °F
|
ASTM D 638 | |
| 0.700 J/cm
@Temperature 23.0 °C
|
1.31 ft-lb/in
@Temperature 73.4 °F
|
ASTM D 256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 135 °C | 275 °F | 120°C/hr; ASTM D 648 |
| Vicat Softening Point | 105 °C
@Load 5.00 kg
|
221 °F
@Load 11.0 lb
|
50°C/hr; ASTM D 1525 |
| Flammability, UL94 | HB
@Thickness 1.60 mm
|
HB
@Thickness 0.0630 in
|
|
| HB
@Thickness 3.20 mm
|
HB
@Thickness 0.126 in
|