Dow H110-02NZ Polypropylene Homopolymer Resin
| Manufacturer | Dow Chemical |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
OverviewContains a nucleating agentGood melt strengthComplies with U.S. FDA 21 CFR 177.1520 (c)3.2aDOW H110-02NZ Polypropylene Resin is intended for use in extrusion and thermoforming processes in opaque applications.Dow Announced Sale of Global Polypropylene Business to Braskem in July 2011.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.900 g/cc | 0.0325 lb/in³ | ASTM D792 |
| Melt Index of Compound | 2.0 g/10 min
@Load 2.16 kg,
Temperature 230 °C |
2.0 g/10 min
@Load 4.76 lb,
Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 35.2 MPa | 5110 psi | ASTM D638 |
| Elongation at Yield | 9.0 % | 9.0 % | ASTM D638 |
| Flexural Modulus, 1% Secant | 1590 MPa | 231000 psi | ASTM D790 |
| Izod Impact, Notched | 0.320 J/cm
@Temperature 0.000 °C
|
0.599 ft-lb/in
@Temperature 32.0 °F
|
ASTM D256A |
| 0.507 J/cm
@Temperature 23.0 °C
|
0.950 ft-lb/in
@Temperature 73.4 °F
|
ASTM D256A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 161 °C | 322 °F | DSC; Dow Method |
| Deflection Temperature at 0.46 MPa (66 psi) | 103 °C | 217 °F | Unannealed; ASTM D648 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 14 % | 14 % | ASTM D1003 |