DuPont Performance Polymers Rynite® FR530 BK507 PET (Unverified Data**)
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Rynite® FR530 BK507 is a 30% glass reinforced, flame retardant, modified polyethylene terephthalate resin.Information provided by DuPont Performance Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.68 g/cc | 0.0607 lb/in³ | ISO 1183 |
| Filler Content | 30 % | 30 % | |
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm
@Thickness 2.00 mm
|
0.0020 in/in
@Thickness 0.0787 in
|
ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm
@Thickness 2.00 mm
|
0.0080 in/in
@Thickness 0.0787 in
|
ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 43.0 MPa
@Temperature 150 °C
|
6240 psi
@Temperature 302 °F
|
ISO 527 |
| 67.0 MPa
@Temperature 90.0 °C
|
9720 psi
@Temperature 194 °F
|
ISO 527 | |
| 130 MPa
@Temperature 23.0 °C
|
18900 psi
@Temperature 73.4 °F
|
ISO 527 | |
| 172 MPa
@Temperature -40.0 °C
|
24900 psi
@Temperature -40.0 °F
|
ISO 527 | |
| Elongation at Break | 1.8 %
@Temperature -40.0 °C
|
1.8 %
@Temperature -40.0 °F
|
ISO 527 |
| 1.9 %
@Temperature 23.0 °C
|
1.9 %
@Temperature 73.4 °F
|
ISO 527 | |
| 3.5 %
@Temperature 90.0 °C
|
3.5 %
@Temperature 194 °F
|
ISO 527 | |
| 4.0 %
@Temperature 150 °C
|
4.0 %
@Temperature 302 °F
|
ISO 527 | |
| Tensile Modulus | 3.65 GPa
@Temperature 150 °C
|
529 ksi
@Temperature 302 °F
|
ISO 527 |
| 5.90 GPa
@Temperature 90.0 °C
|
856 ksi
@Temperature 194 °F
|
ISO 527 | |
| 11.3 GPa
@Temperature 23.0 °C
|
1640 ksi
@Temperature 73.4 °F
|
ISO 527 | |
| 12.0 GPa
@Temperature -40.0 °C
|
1740 ksi
@Temperature -40.0 °F
|
ISO 527 | |
| Flexural Strength | 69.0 MPa
@Temperature 150 °C
|
10000 psi
@Temperature 302 °F
|
ISO 178 |
| 107 MPa
@Temperature 90.0 °C
|
15500 psi
@Temperature 194 °F
|
ISO 178 | |
| 200 MPa
@Temperature 23.0 °C
|
29000 psi
@Temperature 73.4 °F
|
ISO 178 | |
| 262 MPa
@Temperature -40.0 °C
|
38000 psi
@Temperature -40.0 °F
|
ISO 178 | |
| Flexural Modulus | 2.65 GPa
@Temperature 150 °C
|
384 ksi
@Temperature 302 °F
|
ISO 178 |
| 4.65 GPa
@Temperature 90.0 °C
|
674 ksi
@Temperature 194 °F
|
ISO 178 | |
| 10.5 GPa
@Temperature 23.0 °C
|
1520 ksi
@Temperature 73.4 °F
|
ISO 178 | |
| 11.0 GPa
@Temperature -40.0 °C
|
1600 ksi
@Temperature -40.0 °F
|
ISO 178 | |
| Izod Impact, Notched (ISO) | 8.00 kJ/m²
@Temperature -40.0 °C
|
3.81 ft-lb/in²
@Temperature -40.0 °F
|
ISO 180/1A |
| 8.00 kJ/m²
@Temperature -30.0 °C
|
3.81 ft-lb/in²
@Temperature -22.0 °F
|
ISO 180/1A | |
| 8.50 kJ/m²
@Temperature 23.0 °C
|
4.04 ft-lb/in²
@Temperature 73.4 °F
|
ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 34.0 kJ/m²
@Temperature -40.0 °C
|
16.2 ft-lb/in²
@Temperature -40.0 °F
|
ISO 180/1U |
| 35.0 kJ/m²
@Temperature -30.0 °C
|
16.7 ft-lb/in²
@Temperature -22.0 °F
|
ISO 180/1U | |
| 40.0 kJ/m²
@Temperature 23.0 °C
|
19.0 ft-lb/in²
@Temperature 73.4 °F
|
ISO 180/1U | |
| Charpy Impact Unnotched | 3.00 J/cm²
@Temperature -40.0 °C
|
14.3 ft-lb/in²
@Temperature -40.0 °F
|
ISO 179/1eU |
| 3.50 J/cm²
@Temperature -30.0 °C
|
16.7 ft-lb/in²
@Temperature -22.0 °F
|
ISO 179/1eU | |
| 4.00 J/cm²
@Temperature 23.0 °C
|
19.0 ft-lb/in²
@Temperature 73.4 °F
|
ISO 179/1eU | |
| Charpy Impact, Notched | 0.800 J/cm²
@Temperature -40.0 °C
|
3.81 ft-lb/in²
@Temperature -40.0 °F
|
ISO 179/1eA |
| 0.800 J/cm²
@Temperature -30.0 °C
|
3.81 ft-lb/in²
@Temperature -22.0 °F
|
ISO 179/1eA | |
| 0.900 J/cm²
@Temperature 23.0 °C
|
4.28 ft-lb/in²
@Temperature 73.4 °F
|
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 500 µm/m-°C
@Temperature -40.0 – 23.0 °C
|
278 µin/in-°F
@Temperature -40.0 – 73.4 °F
|
ISO 11359-1/-2 |
| 500 µm/m-°C
@Temperature 23.0 – 55.0 °C
|
278 µin/in-°F
@Temperature 73.4 – 131 °F
|
ISO 11359-1/-2 | |
| 500 µm/m-°C
@Temperature 55.0 – 160 °C
|
278 µin/in-°F
@Temperature 131 – 320 °F
|
ISO 11359-1/-2 | |
| CTE, linear, Transverse to Flow | 73.0 µm/m-°C
@Temperature -40.0 – 23.0 °C
|
40.6 µin/in-°F
@Temperature -40.0 – 73.4 °F
|
ISO 11359-1/-2 |
| 90.0 µm/m-°C
@Temperature 23.0 – 55.0 °C
|
50.0 µin/in-°F
@Temperature 73.4 – 131 °F
|
ISO 11359-1/-2 | |
| 121 µm/m-°C
@Temperature 55.0 – 160 °C
|
67.2 µin/in-°F
@Temperature 131 – 320 °F
|
ISO 11359-1/-2 | |
| Melting Point | 252 °C | 486 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 243 °C | 469 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 220 °C | 428 °F | ISO 75-1/-2 |
| UL RTI, Electrical | 155 °C
@Thickness 0.350 mm
|
311 °F
@Thickness 0.0138 in
|
UL 746B |
| 155 °C
@Thickness 0.750 mm
|
311 °F
@Thickness 0.0295 in
|
UL 746B | |
| 155 °C
@Thickness 1.50 mm
|
311 °F
@Thickness 0.0591 in
|
UL 746B | |
| 155 °C
@Thickness 2.00 mm
|
311 °F
@Thickness 0.0787 in
|
UL 746B | |
| 155 °C
@Thickness 3.00 mm
|
311 °F
@Thickness 0.118 in
|
UL 746B | |
| UL RTI, Mechanical with Impact | 155 °C
@Thickness 2.00 mm
|
311 °F
@Thickness 0.0787 in
|
UL 746B |
| 155 °C
@Thickness 3.00 mm
|
311 °F
@Thickness 0.118 in
|
UL 746B | |
| 155 °C
@Thickness 1.50 mm
|
311 °F
@Thickness 0.0591 in
|
UL 746B | |
| 155 °C
@Thickness 0.750 mm
|
311 °F
@Thickness 0.0295 in
|
UL 746B | |
| UL RTI, Mechanical without Impact | 155 °C
@Thickness 0.750 mm
|
311 °F
@Thickness 0.0295 in
|
UL 746B |
| 155 °C
@Thickness 1.50 mm
|
311 °F
@Thickness 0.0591 in
|
UL 746B | |
| 155 °C
@Thickness 2.00 mm
|
311 °F
@Thickness 0.0787 in
|
UL 746B | |
| 155 °C
@Thickness 3.00 mm
|
311 °F
@Thickness 0.118 in
|
UL 746B | |
| Flammability, UL94 | V-0
@Thickness 2.00 mm
|
V-0
@Thickness 0.0787 in
|
UL94 |
| V-0
@Thickness 1.50 mm
|
V-0
@Thickness 0.0591 in
|
UL94 | |
| V-0
@Thickness 0.750 mm
|
V-0
@Thickness 0.0295 in
|
UL94 | |
| V-0
@Thickness 0.350 mm
|
V-0
@Thickness 0.0138 in
|
UL94 | |
| V-0
@Thickness 3.00 mm
|
V-0
@Thickness 0.118 in
|
IEC 60695-11-10 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | 225 V
@Temperature 23.0 °C
|
225 V
@Temperature 73.4 °F
|
IEC 60112 |
| 250 V
@Temperature 23.0 °C
|
250 V
@Temperature 73.4 °F
|
UL 746A | |
| 250 – 400 V
@Temperature 23.0 °C
|
250 – 400 V
@Temperature 73.4 °F
|
UL 746A |