Eastman Neostar FN005 Elastomer
| Manufacturer | Eastman Chemical |
| Trade Name | Neostar |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Neostar FN005 elastomer is a tough, clear, durable copolyester ether. It was designed for use in the profile and automotive markets, but is also used in packaging and tubing applications where toughness and flex-crack resistance are required. Neostar FN005 can be used in injection molding and cast film or tubing extrusion applications or in any application that demands strength, durability, and puncture resistance in harsh environments. This copolyester combines toughness, clarity, and flexibility without the addition of plasticizers. Neostar FN005 is considered environmentally preferred because of its non-halogenated material composition. The target inherent viscosity of this product is 1.05.Applications/UsesAutomotiveFlexible hingesPricing channelsRetail pricing finsDriver and passenger side air bagsPackagingProfilesTubingKey AttributesEnvironmentally preferred, non-halogenated materialExcellent chemical resistanceExceptional heat resistance and high temperature dimensional stabilityHigh flexibility without plasticizersSolvent bondable
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.13 g/cc | 1.13 g/cc | ASTM D792 |
| Water Absorption | 0.35 % | 0.35 % | 24h Immersion; ASTM D570 |
| Viscosity Measurement | 1.05 | 1.05 | Inherent; EMN-A-AC-G-V-1 |
| Melt Flow | 20 g/10 min
@Load 2.16 kg,
Temperature 230 °C |
20 g/10 min
@Load 4.76 lb,
Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 95 | 95 | ASTM D2240 |
| Hardness, Shore D | 55 | 55 | ASTM D2240 |
| Tensile Strength at Break | 20.0 MPa | 2900 psi | ASTM D638 |
| Tensile Strength, Yield | 14.0 MPa | 2030 psi | ASTM D638 |
| Elongation at Break | 300 % | 300 % | ASTM D638 |
| Elongation at Yield | 30 % | 30 % | ASTM D638 |
| Tensile Modulus | 0.170 GPa | 24.7 ksi | ASTM D638 |
| Flexural Modulus | 0.150 GPa | 21.8 ksi | ASTM D790 |
| Izod Impact, Notched | 0.500 J/cm
@Temperature -40.0 °C
|
0.937 ft-lb/in
@Temperature -40.0 °F
|
ASTM D256 |
| Tear Strength, Total | 370 N | 83.2 lb (f) | ASTM D1004 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Heat of Fusion | 27.0 J/g | 11.6 BTU/lb | ASTM E793 |
| CTE, linear | 150 µm/m-°C
@Temperature 20.0 °C
|
83.3 µin/in-°F
@Temperature 68.0 °F
|
ASTM D696 |
| Specific Heat Capacity | 1.60 J/g-°C | 0.382 BTU/lb-°F | DSC |
| 1.80 J/g-°C
@Temperature 100 °C
|
0.430 BTU/lb-°F
@Temperature 212 °F
|
DSC | |
| 2.00 J/g-°C
@Temperature 150 °C
|
0.478 BTU/lb-°F
@Temperature 302 °F
|
DSC | |
| 2.30 J/g-°C
@Temperature 175 °C
|
0.550 BTU/lb-°F
@Temperature 347 °F
|
solid; DSC | |
| 2.30 J/g-°C
@Temperature 225 °C
|
0.550 BTU/lb-°F
@Temperature 437 °F
|
melt; DSC | |
| 3.10 J/g-°C
@Temperature 200 °C
|
0.741 BTU/lb-°F
@Temperature 392 °F
|
transition; DSC | |
| Thermal Conductivity | 0.190 W/m-K | 1.32 BTU-in/hr-ft²-°F | ASTM C177 |
| Melting Point | 207 °C | 405 °F | Crystalline Peak Melting Point; ASTM D3418 |
| Crystallization Temperature | 140 °C | 284 °F | on cooling; DSC |
| Vicat Softening Point | 170 °C | 338 °F | 1kg load; ASTM D1525 |
| Brittleness Temperature | <= -75.0 °C | <= -103 °F | ASTM D746 |
| Glass Transition Temp, Tg | -3.00 °C | 26.6 °F | DSC |
| Clash Berg Stiffness Temperature | <= -70.0 °C | <= -94.0 °F | at 930 MPa; ASTM D1043 |
| -28.0 °C | -18.4 °F | at 240 MPa; ASTM D1043 |