Eurotec® Tecodur® PB70 GR30 NL CA 01 PBT/PET 30% glass fiber reinforced
| Manufacturer | Eurotec |
| Trade Name | Tecodur® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Excellent stiffness and hardnessGood mechanical strengthGood creep and fatigue behaviorVery good thermal stabilityExcellent flammability characteristicsGood electrical propertiesHigh wear resistance and low frictionGood dimensional stabilityVery good chemical resistanceExcellent flow and processing propertiesLow moisture absorptionVery good surface finishAPPLICATIONS: AutomotiveElectrical/ElectronicBusiness equipmentConstructionHome appliances
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.55 g/cc | 0.0560 lb/in³ | ISO 1183 |
| Filler Content | 30 % | 30 % | ISO 3451 |
| Moisture Absorption at Equilibrium | 0.14 % | 0.14 % | Humidity Absorption, 50% RH, 23°C; ISO 62 |
| Water Absorption at Saturation | 0.35 % | 0.35 % | 23°C; ISO 62 |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | |
| Linear Mold Shrinkage, Transverse | 0.010 cm/cm | 0.010 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 140 MPa | 20300 psi | ISO 527 |
| Elongation at Break | 2.5 % | 2.5 % | ISO 527 |
| Tensile Modulus | 10.0 GPa | 1450 ksi | ISO 527 |
| Flexural Strength | 200 MPa | 29000 psi | ISO 178 |
| Flexural Modulus | 8.50 GPa | 1230 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m²
@Temperature -30.0 °C
|
3.81 ft-lb/in²
@Temperature -22.0 °F
|
ISO 180/1A |
| 10.0 kJ/m²
@Temperature 23.0 °C
|
4.76 ft-lb/in²
@Temperature 73.4 °F
|
ISO 180/1A | |
| Charpy Impact Unnotched | 4.50 J/cm²
@Temperature -30.0 °C
|
21.4 ft-lb/in²
@Temperature -22.0 °F
|
ISO 179/eU |
| 5.00 J/cm²
@Temperature 23.0 °C
|
23.8 ft-lb/in²
@Temperature 73.4 °F
|
ISO 179/eU | |
| Charpy Impact, Notched | 0.900 J/cm²
@Temperature -30.0 °C
|
4.28 ft-lb/in²
@Temperature -22.0 °F
|
ISO 179/eA |
| 1.10 J/cm²
@Temperature 23.0 °C
|
5.24 ft-lb/in²
@Temperature 73.4 °F
|
ISO 179/eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 225 – 250 °C | 437 – 482 °F | 10 K/min; ISO 3146 |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 75-1/2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | ISO 75-1/2 |
| Vicat Softening Point | 210 °C | 410 °F | 50N; ISO 306 |
| Flammability, UL94 | HB
@Thickness 1.60 mm
|
HB
@Thickness 0.0630 in
|
|
| HB
@Thickness 3.20 mm
|
HB
@Thickness 0.126 in
|
||
| Glow Wire Test | 650 °C
@Thickness 2.00 mm
|
1200 °F
@Thickness 0.0787 in
|
plaque; IEC 60695 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | IEC 60093 |
| Comparative Tracking Index | 500 V | 500 V | IEC 60112 |