ExxonMobil Bicor™ 30MBT666 OPP Film
| Manufacturer | Exxon Chemical |
| Trade Name | Bicor™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Product Description: A biaxially oriented transparent polypropylene film, acrylic coated two sides. This film is specifically suitable for unsupported overwrapping, offering unique aspect and cost reduction advantage.Availability: Africa & Middle East, Asia Pacific and EuropeKey Features:Low sealing thresholdHigh seal strength even under low pressure sealingExcellent packaging machine performanceOutstanding optical propertiesNo seal compatibility between acrylic coating and coex filmWater-based coatingsFeatures:Acrylic CoatedFlavor & Aroma BarrierIn Lamination Lap SealableApplications:Box OverwrapTobacco Uses: Tobacco Overwrap Flexible PackagingProcessing Method: Solvent Flexographic Printing, Solvent Rotogravure Printing and Surface Print UnsupportedInformation provided by ExxonMobil
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Water Vapor Transmission | 1.01 g/m²/day
@Temperature 23.0 °C
|
0.0650 g/100 in²/day
@Temperature 73.4 °F
|
85% RH; ExxonMobil Method |
| 4.50 g/m²/day
@Temperature 38.0 °C
|
0.290 g/100 in²/day
@Temperature 100 °F
|
90% RH; ExxonMobil Method | |
| Oxygen Transmission Rate | 751 cc/m²/day
@Temperature 23.0 °C
|
48.4 cc/100 in²/day
@Temperature 73.4 °F
|
0% RH; ExxonMobil Method |
| Thickness | 30.5 microns | 1.20 mil | ExxonMobil Method |
| Coating Weight | 27.7 g/m² | 17.3 lb/ream | ExxonMobil Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 175 % | 175 % | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Film Elongation at Break, TD | 60 % | 60 % | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Modulus of Elasticity | 2.00 GPa | 290 ksi | MD; ExxonMobil Method |
| 3.80 GPa | 551 ksi | TD; ExxonMobil Method | |
| Coefficient of Friction | 0.25 | 0.25 | Both Sides; ExxonMobil Method |
| Seal Strength | 200 g/25 mm
@Pressure 0.00345 MPa,
Temperature 100 °C |
200 g/in
@Pressure 0.500 psi,
Temperature 212 °F |
LPS, 0.5 sec; ExxonMobil Method |
| Film Tensile Strength at Break, MD | 160 MPa | 23200 psi | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Film Tensile Strength at Break, TD | 290 MPa | 42100 psi | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Shrinkage, MD | 6.0 %
@Temperature 135 °C,
Time 432 sec |
6.0 %
@Temperature 275 °F,
Time 0.120 hour |
ExxonMobil Method |
| Shrinkage, TD | 5.5 %
@Temperature 135 °C,
Time 432 sec |
5.5 %
@Temperature 275 °F,
Time 0.120 hour |
ExxonMobil Method |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 1.3 % | 1.3 % | ExxonMobil Method |
| Gloss | 85 % | 85 % | 45°; ExxonMobil Method |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Heat Seal Range | 90°F | 36.3 psi, 0.2 sec |
| Yield | 25000 in2/lb |