ExxonMobil Bicor® 85 AXT OPP Film
| Manufacturer | Exxon Chemical |
| Trade Name | Bicor® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Product Description: Bicor ASB-X is a two side coated, sealable OPP film delivering an advanced level of moisture and oxygen battier protection. This film is designed for use in (unsupported and surface printed) horizontal or vertical packaging applications. It is also used as an outer web of laminations for vertical gas-flush applications.Availability: Latin America, North America and South AmericaKey Features:Robust machinabilityLow and consistent COFExcellent barrier performanceOutstanding flavor and aroma barrierExcellent moisture barrierExcellent oxygen barrierFeatures:Acrylic CoatedFlavor & Aroma BarrierGas BarrierHigh Barrier Printable PVdC CoatedHigh Barrier PVdC CoatedIn Lamination Lap SealableMoisture BarrierOxygen BarrierPVdC CoatedSealable High Barrier PVdC CoatedApplications:BakeryBiscuits/Cookie/CrackersBox OverwrapConfectionery, GumConfectionery, SugarPet FoodUses:Box Overwrap Flexible PackagingHFFS Flexible PackagingPre-made Bags – Flexible PackagingVFFS Flexible PackagingProcessing Method: Cold Seal Adhesive, Inner Web Adhesive Lamination, Outer Web Adhesive Lamination, Outer Web Extrusion Lamination, Solvent Flexographic Printing, Solvent Rotogravure Printing, Surface Print Unsupported and Water-based Flexographic Printing Information provided by ExxonMobil Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Water Vapor Transmission | 3.10 g/m²/day | 0.200 g/100 in²/day | 38°C, 90% RH; ExxonMobil Method |
| Oxygen Transmission Rate | 6.20 cc/m²/day | 0.399 cc/100 in²/day | 23°C, 0% RH; ExxonMobil Method |
| Thickness | 20.8 microns | 0.820 mil | Nominal; ExxonMobil Method |
| Coating Weight | 19.7 g/m² | 12.3 lb/ream | ExxonMobil Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Coefficient of Friction | 0.29 | 0.29 | Acrylic/Acrylic; ExxonMobil Method |
| Film Tensile Strength at Break, MD | 117 MPa | 17000 psi | 20 in/min, 2.0 in Jaw Separation; ExxonMobil Method |
| Film Tensile Strength at Break, TD | 207 MPa | 30000 psi | 20 in/min, 2.0 in Jaw Separation; ExxonMobil Method |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Shrinkage, MD | 4.5 % | 4.5 % | at 275°F; ExxonMobil Method |
| Shrinkage, TD | 3.0 % | 3.0 % | at 275°F; ExxonMobil Method |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 1.5 % | 1.5 % | ExxonMobil Method |
| Gloss | 103 % | 103 % | 45º; ExxonMobil Method |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Crimp Seal MST | 207°F | PVdC/PVdC, 200g/in |
| Crimp Seal Strength | 600 g/in | PVdC/PVdC, 260°F, 20psi, 3/4sec |
| Yield | 35000 in2/lb |