ExxonMobil Label-Lyte™ 50LH247 OPP Film
| Manufacturer | Exxon Chemical |
| Trade Name | Label-Lyte™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Product Description: A super white opaque, cavitated BOPP film for Pressure Sensitive (PSA) labeling applications where superior optics are desired. 50LH247 also shows excellent performances on reel-fed wrap-around labeling machines, where its high stiffness is particularly appreciated.Availability: Africa & Middle East, Asia Pacific and EuropeKey Features:Outstanding white opaque background and superb white gloss finishGood printability on outside treated sideCompatibility with most adhesive formulationsExcellent stiffness and flex resistanceVery good moisture resistanceGood overall converting, diecutting and dispensing propertiesApplications: Dairy Products IndustrialUses: Pressure Sensitive Labels Reel-Fed LabelsProcessing Method: Inner Web Adhesive Lamination, Solvent Flexographic Printing, Solvent Rotogravure Printing, Surface Print Unsupported, UV Flexographic Printing, UV Letterpress Printing, UV Offset Lithography Printing and Water-based Flexographic PrintingInformation provided by ExxonMobil
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Thickness | 50.8 microns | 2.00 mil | ExxonMobil Method |
| Coating Weight | 35.7 g/m² | 22.3 lb/ream | ExxonMobil Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 170 % | 170 % | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Film Elongation at Break, TD | 55 % | 55 % | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Modulus of Elasticity | 1.70 GPa | 247 ksi | MD; ExxonMobil Method |
| 2.80 GPa | 406 ksi | TD; ExxonMobil Method | |
| Coefficient of Friction | 0.60 | 0.60 | Untreated Surface; ExxonMobil Method |
| Film Tensile Strength at Break, MD | 105 MPa | 15200 psi | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Film Tensile Strength at Break, TD | 185 MPa | 26800 psi | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Shrinkage, MD | 3.0 %
@Temperature 135 °C,
Time 432 sec |
3.0 %
@Temperature 275 °F,
Time 0.120 hour |
ExxonMobil Method |
| Shrinkage, TD | 3.0 %
@Temperature 135 °C,
Time 432 sec |
3.0 %
@Temperature 275 °F,
Time 0.120 hour |
ExxonMobil Method |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Gloss | 70 % | 70 % | 45°; ExxonMobil Method |
| Transmission, Visible | 22 % | 22 % | ExxonMobil Method |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Yield | 19300 in2/lb |