ExxonMobil Metallyte™ 38ICE M OPP Film
| Manufacturer | Exxon Chemical |
| Trade Name | Metallyte™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Product Description: A coextruded super white opaque, low density, biaxially oriented polypropylene film, metalized on one side. This film is designed for HFFS applications, heat seal or cold seal.Availability: Africa & Middle East, Asia Pacific and EuropeKey Features:High yieldOutstanding opacity and light barrierBrilliant metal appearance on one side, bright white background on the other sideWell adapted to cold seal processHigh SOF inside to optimize line efficiency (product positioning)Metal surface must be varnished to be protectedFeatures:Light BarrierApplications:Frozen FoodIce Cream Uses: HFFS Flexible PackagingProcessing Method: Cold Seal Adhesive, Solvent Flexographic Printing, Solvent Rotogravure Printing and Surface Print UnsupportedInformation provided by ExxonMobil
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Thickness | 38.1 microns | 1.50 mil | ExxonMobil Method |
| Coating Weight | 23.2 g/m² | 14.5 lb/ream | ExxonMobil Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 140 % | 140 % | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Film Elongation at Break, TD | 50 % | 50 % | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Modulus of Elasticity | 1.30 GPa | 189 ksi | MD; ExxonMobil Method |
| 2.10 GPa | 305 ksi | TD; ExxonMobil Method | |
| Seal Strength | 360 g/25 mm
@Pressure 0.276 MPa,
Temperature 140 °C |
360 g/in
@Pressure 40.0 psi,
Temperature 284 °F |
Otto Brugger, 0.2 sec; ExxonMobil Method |
| Film Tensile Strength at Break, MD | 100 MPa | 14500 psi | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Film Tensile Strength at Break, TD | 155 MPa | 22500 psi | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Shrinkage, MD | 6.0 %
@Temperature 135 °C,
Time 432 sec |
6.0 %
@Temperature 275 °F,
Time 0.120 hour |
ExxonMobil Method |
| Shrinkage, TD | 6.0 %
@Temperature 135 °C,
Time 432 sec |
6.0 %
@Temperature 275 °F,
Time 0.120 hour |
ExxonMobil Method |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Optical Density | 3.6 | 3.6 | ExxonMobil Method |
| Gloss | 75 % | 75 % | 45°; ExxonMobil Method |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Heat Seal Range | 54°F | 36.3 psi, 0.2 sec |
| Yield | 29800 in2/lb |