ExxonMobil Metallyte™ UHB 35 MWHB OPP Film
| Manufacturer | Exxon Chemical |
| Trade Name | Metallyte™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Product Description: A multi-layer, cavitaed, white OPP film structure that has exceptional barrier to gases and flavors. It is metalized on one side and treated on the other. It is designed for use in laminations or as a converted monoweb, especially with converter-applied cold seal sealants. The treated face has surface sealing characteristics for fine sealing and will lap seal to some coextruded OPP films.Availability: Latin America, North America and South AmericaKey Features:Outstanding opacityOutstanding moisture and oxygen barrierOutstanding aroma and flavor barrierExcellent flex-Crack resistanceExcellent surface for high graphic qualityFeatures:Flavor & Aroma BarrierGas Barrier In Lamination Lap SealableLight BarrierMoisture BarrierOxygen BarrierApplications:Bakery Uses: HFFS Flexible Packaging Pouches – Flexible PackagingPre-made Bags – Flexible PackagingVFFS Flexible PackagingProcessing Method: Cold Seal Adhesive, Extrusion Coating, Inner Web Adhesive Lamination, Inner Web Extrusion Lamination, Solvent Flexographic Priming, Solvent Rotogravure Printing, Surface Print Unsupported and Water-based Flexographic PrintingInformation provided by ExxonMobil
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Water Vapor Transmission | 0.295 g/m²/day
@Temperature 38.0 °C
|
0.0190 g/100 in²/day
@Temperature 100 °F
|
90% RH; ExxonMobil Method |
| Oxygen Transmission Rate | 0.0931 cc/m²/day | 0.00600 cc/100 in²/day | ExxonMobil Method |
| Thickness | 35.6 microns | 1.40 mil | ExxonMobil Method |
| Coating Weight | 24.8 g/m² | 15.5 lb/ream | ExxonMobil Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Break, MD | 75.2 MPa | 10900 psi | 20 in/min, 2.0 in Jaw Separation; ExxonMobil Method |
| Film Tensile Strength at Break, TD | 84.8 MPa | 12300 psi | 20 in/min, 2.0 in Jaw Separation; ExxonMobil Method |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Shrinkage, MD | 5.0 %
@Temperature 135 °C
|
5.0 %
@Temperature 275 °F
|
ExxonMobil Method |
| Shrinkage, TD | 5.0 %
@Temperature 135 °C
|
5.0 %
@Temperature 275 °F
|
ExxonMobil Method |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Treatment | 40 dyne/cm | Treated Surface |
| Yield | 27900 in2/lb |