Fibre Glast Saf-T-Poxy 2410 / 2184 Epoxy (discontinued **)
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Information provided by Fibre Glast Developments Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | |
| Viscosity | 800 cP | 800 cP | ASTM D2293 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 85 | 85 | Cured; ASTM D2240 |
| Tensile Strength at Break | 268.5 MPa | 38940 psi | Property derived with 10 Ply Laminate, hand Lay-up, Style 181 Glass Fabric, 55% Glass Content.; ASTM D638 |
| Elongation at Break | 2.04 % | 2.04 % | Property derived with 10 Ply Laminate, hand Lay-up, Style 181 Glass Fabric, 55% Glass Content.; ASTM D638 |
| Tensile Modulus | 14.8 GPa | 2140 ksi | Property derived with 10 Ply Laminate, hand Lay-up, Style 181 Glass Fabric, 55% Glass Content. |
| Flexural Strength | 289.77 MPa | 42028 psi | Property derived with 10 Ply Laminate, hand Lay-up, Style 181 Glass Fabric, 55% Glass Content.; ASTM D790 |
| Flexural Modulus | 15.4 GPa | 2240 ksi | Property derived with 10 Ply Laminate, hand Lay-up, Style 181 Glass Fabric, 55% Glass Content.; ASTM D790 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Glass Transition Temp, Tg | 83.3 °C | 182 °F |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Pot Life | 120 min
@Temperature 25.0 °C
|
120 min
@Temperature 77.0 °F
|
4 fl. Oz.; ASTM D2471 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Mix Ratio | 100:44 | Resin:Hardener by Weight |
| 2.13:1 | Resin:Hardener by Volume |