Description
Material Notes:
Description: Machining grade with good electrical properties and moisture resistance. Low cold flow with good dimensional stability. Thickness Tested: 0.062″, 0.125″, and 0.500″
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.35 – 1.45 g/cc
@Thickness 1.57 mm
|
1.35 – 1.45 g/cc
@Thickness 0.0620 in
|
ASTM D792 |
| Moisture Absorption at Equilibrium | 1.3 %
@Thickness 1.57 mm
|
1.3 %
@Thickness 0.0620 in
|
ASTM D229 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 90 – 110
@Thickness 1.57 mm
|
90 – 110
@Thickness 0.0620 in
|
ASTM D785 |
| Tensile Strength, Yield | 82.7 MPa
@Thickness 1.57 mm
|
12000 psi
@Thickness 0.0620 in
|
CW; ASTM D638 |
| 96.5 MPa
@Thickness 1.57 mm
|
14000 psi
@Thickness 0.0620 in
|
LW; ASTM D638 | |
| Modulus of Elasticity | 7.24 GPa
@Thickness 1.57 mm
|
1050 ksi
@Thickness 0.0620 in
|
CW; ASTM D229 |
| 8.96 GPa
@Thickness 1.57 mm
|
1300 ksi
@Thickness 0.0620 in
|
LW; ASTM D229 | |
| Flexural Strength | 103 MPa
@Thickness 1.57 mm
|
15000 psi
@Thickness 0.0620 in
|
CW; ASTM D790 |
| 138 MPa
@Thickness 1.57 mm
|
20000 psi
@Thickness 0.0620 in
|
LW; ASTM D790 | |
| Compressive Strength | 207 MPa
@Thickness 12.7 mm
|
30000 psi
@Thickness 0.500 in
|
ASTM D695 |
| Shear Strength | 88.3 MPa
@Thickness 15.7 mm
|
12800 psi
@Thickness 0.620 in
|
ASTM D732 |
| Izod Impact, Unnotched | 0.240 J/cm
@Thickness 12.7 mm
|
0.450 ft-lb/in
@Thickness 0.500 in
|
CW, Cond E-48/50; ASTM D256 |
| 0.294 J/cm
@Thickness 12.7 mm
|
0.550 ft-lb/in
@Thickness 0.500 in
|
LW, Cond E-48/50; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 19.0 µm/m-°C
@Thickness 1.57 mm,
Temperature 20.0 °C |
10.6 µin/in-°F
@Thickness 0.0620 in,
Temperature 68.0 °F |
x-axis; IPC-TM 650-2.4.24 |
| CTE, linear, Transverse to Flow | 15.0 µm/m-°C
@Thickness 1.57 mm,
Temperature 20.0 °C |
8.33 µin/in-°F
@Thickness 0.0620 in,
Temperature 68.0 °F |
x-axis; IPC-TM 650-2.4.24 |
| Maximum Service Temperature, Air | 130 °C | 266 °F | |
| Flammability, UL94 | HB
@Thickness 1.57 mm
|
HB
@Thickness 0.0620 in
|
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 6.1
@Thickness 1.57 mm
|
6.1
@Thickness 0.0620 in
|
Permittivity, Cond D-24/23; ASTM D150 |
| Dielectric Strength | 23.6 kV/mm
@Thickness 1.57 mm
|
600 kV/in
@Thickness 0.0620 in
|
Cond D-48/50; ASTM D229 S.T. |
| 27.6 kV/mm
@Thickness 1.57 mm
|
700 kV/in
@Thickness 0.0620 in
|
Cond A; ASTM D229 S.T. | |
| Dielectric Breakdown | 10000 V
@Thickness 1.57 mm
|
10000 V
@Thickness 0.0620 in
|
Cond D-48/50; ASTM D229 S/S |
| 40000 V
@Thickness 1.57 mm
|
40000 V
@Thickness 0.0620 in
|
Cond A; ASTM D229 S/S | |
| Dissipation Factor | 0.050
@Thickness 1.57 mm
|
0.050
@Thickness 0.0620 in
|
Cond D-24/23; ASTM D150 |
| Arc Resistance | 110 sec
@Thickness 3.17 mm
|
110 sec
@Thickness 0.125 in
|
ASTM D495 |
| Comparative Tracking Index | 200 V
@Thickness 3.17 mm
|
200 V
@Thickness 0.125 in
|
ASTM D3638 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Bond Strength | 1000 lb | 0.5″, ASTM D229 |
| Color | Natural, Black |