Inno-Comp INNOPOL® CS 1-5120 BLH 20% Talc-Filled Polypropylene Homopolymer
| Manufacturer | Inno-Comp Ltd |
| Trade Name | INNOPOL® CS |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
INNOPOL® CS 1-5120 BLH is a 20% talc-filled polypropylene homopolymer compound /PP-H TD20 (ISO 1043)/.INNOPOL® CS 1-5120 BLH is recommended especially for producing products, where high stiffness and long term heat stability are required.All information provided by INNO-COMP.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc
@Temperature 23.0 °C
|
0.0376 lb/in³
@Temperature 73.4 °F
|
ISO 1183 |
| Melt Flow | 12 g/10 min
@Load 5.00 kg,
Temperature 230 °C |
12 g/10 min
@Load 11.0 lb,
Temperature 446 °F |
ISO 1133 |
| Ash | 20 %
@Temperature 600 °C
|
20 %
@Temperature 1110 °F
|
ISO 3451-1/A |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 31.0 MPa | 4500 psi | 50 mm/min; ISO 527-1,-2 |
| Elongation at Break | 35 % | 35 % | ISO 527-1,-2 |
| Elongation at Yield | 5.5 % | 5.5 % | 50 mm/min; ISO 527-1,-2 |
| Tensile Modulus | 2.50 GPa | 363 ksi | 1 mm/min; ISO 527-1,-2 |
| Flexural Modulus | 2.60 GPa | 377 ksi | 2 mm/min; ISO 178 |
| Charpy Impact Unnotched | 1.50 J/cm²
@Temperature -30.0 °C
|
7.14 ft-lb/in²
@Temperature -22.0 °F
|
ISO 179/1eU |
| 6.50 J/cm²
@Temperature 23.0 °C
|
30.9 ft-lb/in²
@Temperature 73.4 °F
|
ISO 179/1eU | |
| Charpy Impact, Notched | 0.160 J/cm²
@Temperature -30.0 °C
|
0.761 ft-lb/in²
@Temperature -22.0 °F
|
ISO 179/1eA |
| 0.450 J/cm²
@Temperature 23.0 °C
|
2.14 ft-lb/in²
@Temperature 73.4 °F
|
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 112 °C | 234 °F | ISO 75-1,-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | ISO 75-1,-2 |
| Vicat Softening Point | 90.0 °C | 194 °F | B120; ISO 306 |
| 153 °C | 307 °F | A120; ISO 306 | |
| Flammability, UL94 | HB
@Thickness 1.60 mm
|
HB
@Thickness 0.0630 in
|
FMVSS 302 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Black |