Inno-Comp INNOPOL® CS 2-3130 NU UV-Stabilized 30% Talc-Filled Polypropylene Block-Copolymer
| Manufacturer | Inno-Comp Ltd |
| Trade Name | INNOPOL® CS |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
INNOPOL® CS 2-3130 NU is an UV-stabilized 30% talc-filled polypropylene block-copolymer compound /PP-B TD30 (ISO 1043)/.INNOPOL® CS 2-3130 NU is recommended for producing injection molded products where the required property is high strength and high stiffness besides low shrinkage and low-temperature resistance.All information provided by INNO-COMP.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc
@Temperature 23.0 °C
|
0.0408 lb/in³
@Temperature 73.4 °F
|
ISO 1183 |
| Melt Flow | 12 g/10 min
@Load 2.16 kg,
Temperature 230 °C |
12 g/10 min
@Load 4.76 lb,
Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 28.0 MPa | 4060 psi | 50 mm/min; ISO 527-1,-2 |
| Elongation at Yield | 2.7 % | 2.7 % | 50 mm/min; ISO 527-1,-2 |
| Tensile Modulus | 3.10 GPa | 450 ksi | 1 mm/min; ISO 527-1,-2 |
| Flexural Modulus | 3.20 GPa | 464 ksi | 2 mm/min; ISO 178 |
| Charpy Impact, Notched | 0.260 J/cm²
@Temperature -20.0 °C
|
1.24 ft-lb/in²
@Temperature -4.00 °F
|
ISO 179/1eA |
| 0.450 J/cm²
@Temperature 23.0 °C
|
2.14 ft-lb/in²
@Temperature 73.4 °F
|
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 129 °C | 264 °F | ISO 75-1,-2 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Natural |