LATI Lasulf G/30 PSU, 30% Glass Fiber Reinforced
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Polysulfone (PSU) based compound. Glass fibers. Low smoke density and low toxicity index. Very high dimensional stabilityAvailability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.47 g/cc | 0.0531 lb/in³ | |
| Linear Mold Shrinkage, Flow | 0.0010 – 0.0030 cm/cm | 0.0010 – 0.0030 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0045 – 0.0060 cm/cm | 0.0045 – 0.0060 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 70.0 MPa
@Temperature 150 °C
|
10200 psi
@Temperature 302 °F
|
|
| 80.0 MPa
@Temperature 120 °C
|
11600 psi
@Temperature 248 °F
|
||
| 95.0 MPa
@Temperature 90.0 °C
|
13800 psi
@Temperature 194 °F
|
||
| 110 MPa
@Temperature 60.0 °C
|
16000 psi
@Temperature 140 °F
|
||
| 120 MPa
@Temperature 23.0 °C
|
17400 psi
@Temperature 73.4 °F
|
||
| Elongation at Break | 1.6 %
@Temperature 150 °C
|
1.6 %
@Temperature 302 °F
|
|
| 1.7 %
@Temperature 120 °C
|
1.7 %
@Temperature 248 °F
|
||
| 1.8 %
@Temperature 60.0 °C
|
1.8 %
@Temperature 140 °F
|
||
| 1.8 %
@Temperature 90.0 °C
|
1.8 %
@Temperature 194 °F
|
||
| 1.9 %
@Temperature 23.0 °C
|
1.9 %
@Temperature 73.4 °F
|
||
| Tensile Modulus | 7.00 GPa
@Temperature 150 °C
|
1020 ksi
@Temperature 302 °F
|
|
| 7.30 GPa
@Temperature 120 °C
|
1060 ksi
@Temperature 248 °F
|
||
| 7.50 GPa
@Temperature 90.0 °C
|
1090 ksi
@Temperature 194 °F
|
||
| 7.70 GPa
@Temperature 60.0 °C
|
1120 ksi
@Temperature 140 °F
|
||
| 8.00 GPa
@Temperature 23.0 °C
|
1160 ksi
@Temperature 73.4 °F
|
||
| Charpy Impact Unnotched | 3.50 J/cm² | 16.7 ft-lb/in² | |
| Charpy Impact, Notched | 1.00 J/cm² | 4.76 ft-lb/in² |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 160 °C | 320 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 190 °C | 374 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 185 °C | 365 °F | |
| Vicat Softening Point | 185 °C
@Load 5.00 kg
|
365 °F
@Load 11.0 lb
|
|
| Flammability, UL94 | V-0
@Thickness 3.00 mm
|
V-0
@Thickness 0.118 in
|
|
| V-0
@Thickness 1.50 mm
|
V-0
@Thickness 0.0591 in
|
||
| Oxygen Index | 38 % | 38 % | |
| Glow Wire Test | 960 °C
@Thickness 1.00 mm
|
1760 °F
@Thickness 0.0394 in
|
GWFI/GWT |
| 960 °C
@Thickness 2.00 mm
|
1760 °F
@Thickness 0.0787 in
|
GWFI/GWT |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | 125 V | 125 V | A solution |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 300 – 330 °C | 572 – 626 °F | |
| Mold Temperature | 120 – 140 °C | 248 – 284 °F | |
| Drying Temperature | 110 – 130 °C
@Time 10800 sec
|
230 – 266 °F
@Time 3.00 hour
|
| Descriptive Properties | Value | Comments |
|---|---|---|
| ISO Shrinkage – Pressure | 60 MPa |