LATI Latigray 53/22-01 CX/25 PP Homopolymer, Impact Modified `
| Manufacturer | LATI |
| Trade Name | Latigray |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Radiopaque compound based on Polypropylene homopolymer (PPh), impact modified. Special mineral filler.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.11 g/cc | 0.0401 lb/in³ | |
| Linear Mold Shrinkage, Flow | 0.011 – 0.014 cm/cm | 0.011 – 0.014 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0115 – 0.0145 cm/cm | 0.0115 – 0.0145 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 18.0 MPa
@Temperature 23.0 °C
|
2610 psi
@Temperature 73.4 °F
|
|
| Elongation at Break | >= 100 %
@Temperature 23.0 °C
|
>= 100 %
@Temperature 73.4 °F
|
|
| >= 100 %
@Temperature 60.0 °C
|
>= 100 %
@Temperature 140 °F
|
||
| >= 100 %
@Temperature 90.0 °C
|
>= 100 %
@Temperature 194 °F
|
||
| Elongation at Yield | 6.0 %
@Temperature 23.0 °C
|
6.0 %
@Temperature 73.4 °F
|
|
| 8.5 %
@Temperature 60.0 °C
|
8.5 %
@Temperature 140 °F
|
||
| 9.0 %
@Temperature 90.0 °C
|
9.0 %
@Temperature 194 °F
|
||
| Tensile Modulus | 0.650 GPa
@Temperature 90.0 °C
|
94.3 ksi
@Temperature 194 °F
|
|
| 1.10 GPa
@Temperature 60.0 °C
|
160 ksi
@Temperature 140 °F
|
||
| 2.60 GPa
@Temperature 23.0 °C
|
377 ksi
@Temperature 73.4 °F
|
||
| Charpy Impact Unnotched | 1.50 J/cm²
@Temperature -20.0 °C
|
7.14 ft-lb/in²
@Temperature -4.00 °F
|
|
| 6.50 J/cm²
@Temperature 23.0 °C
|
30.9 ft-lb/in²
@Temperature 73.4 °F
|
||
| Charpy Impact, Notched | 0.100 J/cm²
@Temperature -20.0 °C
|
0.476 ft-lb/in²
@Temperature -4.00 °F
|
|
| 0.350 J/cm²
@Temperature 23.0 °C
|
1.67 ft-lb/in²
@Temperature 73.4 °F
|
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 120 °C | 248 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 105 °C | 221 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | |
| Vicat Softening Point | 95.0 °C
@Load 5.00 kg
|
203 °F
@Load 11.0 lb
|
|
| Flammability, UL94 | HB
@Thickness 1.50 mm
|
HB
@Thickness 0.0591 in
|
|
| HB
@Thickness 0.750 mm
|
HB
@Thickness 0.0295 in
|
||
| Oxygen Index | 24 % | 24 % | |
| Glow Wire Test | 750 °C
@Thickness 1.00 mm
|
1380 °F
@Thickness 0.0394 in
|
GWFI/GWT |
| 750 °C
@Thickness 2.00 mm
|
1380 °F
@Thickness 0.0787 in
|
GWFI/GWT |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | 600 V | 600 V | A solution |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 200 – 240 °C | 392 – 464 °F | |
| Mold Temperature | 40.0 – 60.0 °C | 104 – 140 °F | |
| Drying Temperature | 80.0 – 90.0 °C
@Time 10800 sec
|
176 – 194 °F
@Time 3.00 hour
|
| Descriptive Properties | Value | Comments |
|---|---|---|
| ISO Shrinkage – Pressure | 60 MPa |