LATI Latigray 53/22-01 CX/70 PP Homopolymer, Impact Modified
| Manufacturer | LATI |
| Trade Name | Latigray |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Radiopaque compound based on Polypropylene homopolymer (PPh), impact modified. Special mineral filler. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.96 g/cc | 0.0708 lb/in³ | |
| Thickness | 720 microns | 28.3 mil | 80 |
| 840 microns | 33.1 mil | 120 | |
| Linear Mold Shrinkage, Flow | 0.012 – 0.015 cm/cm | 0.012 – 0.015 in/in | |
| Linear Mold Shrinkage, Transverse | 0.017 – 0.020 cm/cm | 0.017 – 0.020 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 15.0 MPa | 2180 psi | |
| Elongation at Break | 1.8 %
@Temperature 23.0 °C
|
1.8 %
@Temperature 73.4 °F
|
|
| Elongation at Yield | 0.90 %
@Temperature 23.0 °C
|
0.90 %
@Temperature 73.4 °F
|
|
| Tensile Modulus | 3.50 GPa | 508 ksi | |
| Charpy Impact Unnotched | 3.00 J/cm² | 14.3 ft-lb/in² | |
| Charpy Impact, Notched | 0.250 J/cm² | 1.19 ft-lb/in² |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 130 °C | 266 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C | 230 °F | |
| Vicat Softening Point | 120 °C
@Load 5.00 kg
|
248 °F
@Load 11.0 lb
|
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 220 – 240 °C | 428 – 464 °F | |
| Mold Temperature | 20.0 – 40.0 °C | 68.0 – 104 °F | |
| Drying Temperature | 80.0 – 100 °C
@Time 10800 sec
|
176 – 212 °F
@Time 3.00 hour
|
| Descriptive Properties | Value | Comments |
|---|---|---|
| ISO Shrinkage – Pressure | 60 MPa |