LG Chemical LUCON TR1000 PMMA+CNT
| Manufacturer | LG Chemical |
| Trade Name | LUCON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Description: Injection Molding, PMMA+CNT, Transparency, Permanent Antistatic, Low OutgassingApplication: Wafer Carrier Cover, Pellicle TrayCAS No. 9010-94-0 and 25053-09-2Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.16 g/cc | 1.16 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0040 – 0.0070 cm/cm
@Thickness 3.20 mm
|
0.0040 – 0.0070 in/in
@Thickness 0.126 in
|
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 54.9 MPa
@Thickness 3.20 mm
|
7970 psi
@Thickness 0.126 in
|
50mm/min; ASTM D638 |
| Elongation at Break | 30 %
@Thickness 3.20 mm
|
30 %
@Thickness 0.126 in
|
50mm/min; ASTM D638 |
| Flexural Yield Strength | 85.3 MPa
@Thickness 3.20 mm
|
12400 psi
@Thickness 0.126 in
|
15mm/min; ASTM D790 |
| Flexural Modulus | 2.16 GPa
@Thickness 3.20 mm
|
313 ksi
@Thickness 0.126 in
|
15mm/min; ASTM D790 |
| Izod Impact, Notched | >= 0.451 J/cm
@Thickness 3.20 mm,
Temperature 23.0 °C |
>= 0.845 ft-lb/in
@Thickness 0.126 in,
Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C
@Thickness 6.40 mm
|
212 °F
@Thickness 0.252 in
|
ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 90.0 °C
@Thickness 6.40 mm
|
194 °F
@Thickness 0.252 in
|
ASTM D648 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 10 % | 10 % | ASTM D1003 |
| Transmission, Visible | 75 % | 75 % | ASTM D1003 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 2.00e+12 ohm | 2.00e+12 ohm | IEC 60093 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 180 – 200 °C | 356 – 392 °F | Injection Molding |
| Middle Barrel Temperature | 190 – 210 °C | 374 – 410 °F | Injection Molding |
| Front Barrel Temperature | 200 – 220 °C | 392 – 428 °F | Injection Molding |
| Nozzle Temperature | 200 – 230 °C | 392 – 446 °F | Injection Molding |
| Melt Temperature | 200 – 230 °C | 392 – 446 °F | Injection Molding |
| Mold Temperature | 40.0 – 60.0 °C | 104 – 140 °F | Injection Molding |
| Drying Temperature | 70.0 – 80.0 °C | 158 – 176 °F | Injection Molding |
| Dry Time | 2.00 – 4.00 hour | 2.00 – 4.00 hour | Injection Molding |
| Back Pressure | 0.490 – 0.981 MPa | 71.1 – 142 psi | Injection Molding |
| Screw Speed | <= 80 rpm | <= 80 rpm | Injection Molding |