LG Chemical LUPOL HM2300 PP+GF30%
| Manufacturer | LG Chemical |
| Trade Name | LUPOL |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Description: Injection Molding, PP+GF30%, Good WeatherabilityApplication: Electrical, Electronic and Automotive Parts CAS: 9003-07-0 and 65997-17-3Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.15 g/cc | 1.15 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.010 | 0.010 | Injection Molding |
| Linear Mold Shrinkage, Flow | 0.0020 – 0.0040 cm/cm
@Thickness 3.20 mm
|
0.0020 – 0.0040 in/in
@Thickness 0.126 in
|
ASTM D955 |
| Melt Flow | 8.0 g/10 min
@Load 2.16 kg,
Temperature 230 °C |
8.0 g/10 min
@Load 4.76 lb,
Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 85.8 MPa
@Thickness 3.20 mm
|
12400 psi
@Thickness 0.126 in
|
50mm/min; ASTM D638 |
| Elongation at Break | 7.0 %
@Thickness 3.20 mm
|
7.0 %
@Thickness 0.126 in
|
50mm/min; ASTM D638 |
| Flexural Yield Strength | 118 MPa
@Thickness 6.40 mm
|
17100 psi
@Thickness 0.252 in
|
30mm/min; ASTM D790 |
| Flexural Modulus | 5.49 GPa
@Thickness 6.40 mm
|
797 ksi
@Thickness 0.252 in
|
30mm/min; ASTM D790 |
| Izod Impact, Notched | >= 0.785 J/cm
@Thickness 6.40 mm,
Temperature 23.0 °C |
>= 1.47 ft-lb/in
@Thickness 0.252 in,
Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 157 °C
@Thickness 3.20 mm
|
315 °F
@Thickness 0.126 in
|
Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 190 – 210 °C | 374 – 410 °F | Injection Molding |
| Middle Barrel Temperature | 200 – 230 °C | 392 – 446 °F | Injection Molding |
| Front Barrel Temperature | 200 – 230 °C | 392 – 446 °F | Injection Molding |
| Nozzle Temperature | 210 – 230 °C | 410 – 446 °F | Injection Molding |
| Melt Temperature | 200 – 230 °C | 392 – 446 °F | Injection Molding |
| Mold Temperature | 40.0 – 60.0 °C | 104 – 140 °F | Injection Molding |
| Drying Temperature | 70.0 – 80.0 °C | 158 – 176 °F | Injection Molding |
| Dry Time | 3.00 – 4.00 hour | 3.00 – 4.00 hour | Injection Molding |
| Back Pressure | 29.4 – 58.8 MPa | 4260 – 8530 psi | Injection Molding |
| Screw Speed | 30 – 60 rpm | 30 – 60 rpm | Injection Molding |