Lucent Polymers TPP-320 Polypropylene, 20% Talc Filled, Impact Modified
| Manufacturer | Lucent Polymers |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Melt Flow Adjustable for ApplicationAdd “U” for UV StabilizedAdd “H” for Heat StabilizedInformation provided by Lucent Polymers, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.05 g/cc | 1.05 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.012 cm/cm
@Thickness 3.17 mm
|
0.012 in/in
@Thickness 0.125 in
|
1/8″ Section |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 26.21 MPa | 3801 psi | ASTM D638 |
| Elongation at Break | >= 10 % | >= 10 % | ASTM D638 |
| Flexural Strength | 44.14 MPa | 6402 psi | ASTM D790 |
| Flexural Modulus | 1.517 GPa | 220.1 ksi | ASTM D790 |
| Izod Impact, Notched | 1.335 J/cm
@Thickness 3.17 mm
|
2.501 ft-lb/in
@Thickness 0.125 in
|
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 71.11 °C | 160.0 °F | ASTM D648 |